NOVA Chemicals Sclair® 11D1 Butene LLDPE Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Sclair® 11D1 Butene LLDPE Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Film Properties. Features: Strength and toughness, good sealing properties, suitable for narrow die gaps.Applications: Industrial packaging, heavy duty sacks.Data provided by the manufacturer.
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ASTM D792
Melt Flow 0.57 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.57 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.0 MPa
1450 psi
ASTM D882
Film Tensile Strength at Yield, TD 10.0 MPa
1450 psi
ASTM D882
Film Elongation at Break, MD 600 %
600 %
ASTM D882
Film Elongation at Break, TD 830 %
830 %
ASTM D882
Secant Modulus, MD 0.200 GPa
29.0 ksi
ASTM D882
Secant Modulus, TD 0.220 GPa
31.9 ksi
ASTM D882
Coefficient of Friction >= 0.50
>= 0.50
ASTM D1894
Elmendorf Tear Strength, MD 6.00 g/micron
152 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 12.0 g/micron
305 g/mil
ASTM D1922
Dart Drop 4.00 g/micron
102 g/mil
F 50; ASTM D1709/A
Film Tensile Strength at Break, MD 35.0 MPa
5080 psi
ASTM D882
Film Tensile Strength at Break, TD 32.0 MPa
4640 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 98.0 °C
208 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 9.0 %

@Thickness 0.0250 mm
9.0 %

@Thickness 0.000984 in
ASTM D1003
Gloss 55 %
55 %
45°; 1 mil; ASTM D1894
Processing Properties Metric English Comments
Melt Temperature 195 - 220 °C
383 - 428 °F