AK Steel ASTM A 424 Type II, VIT-PLUS® DS Enameling Carbon Steel

Category	Metal , Ferrous Metal , Carbon Steel , Low Carbon Steel
Manufacturer	AK Steel
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	AK Steel ASTM A 424 Type II, VIT-PLUS® DS Enameling Carbon Steel.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

VIT-PLUS is a controlled chemistry, non-decarburized steel designed to replace certain types of ingot products. It has good strength after fire properties. It is not recommended for direct-on cover coat porcelain enamel applications. VIT-PLUS is free of fishscale regardless of the enamelInformation provided by AK Steel

Physical Properties	Metric	English	Comments
Density	7.87 g/cc	0.284 lb/in³

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	311 MPa	45100 psi	.0275 - .035 inches sheet thickness; ASTM A 370
Tensile Strength, Yield	198 MPa	28700 psi	.0275 - .035 inches sheet thickness; ASTM A 370
Elongation at Break	43 %	43 %	in 2 inches; ASTM A 370
Modulus of Elasticity	200 GPa	29000 ksi

Thermal Properties	Metric	English
CTE, linear	12.4 µm/m-°C @Temperature 20.0 - 100 °C	6.89 µin/in-°F @Temperature 68.0 - 212 °F
Specific Heat Capacity	0.481 J/g-°C @Temperature 50.0 - 100 °C	0.115 BTU/lb-°F @Temperature 122 - 212 °F
Thermal Conductivity	89.0 W/m-K	618 BTU-in/hr-ft²-°F

Component Elements Properties	Metric	English	Comments
Aluminum, Al	0.050 %	0.050 %
Carbon, C	0.040 %	0.040 %
Copper, Cu	0.020 %	0.020 %
Iron, Fe	99.65 %	99.65 %	As Remainder
Manganese, Mn	0.21 %	0.21 %
Phosphorous, P	0.010 %	0.010 %
Silicon, Si	0.010 %	0.010 %
Sulfur, S	0.010 %	0.010 %

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.0000142 ohm-cm	0.0000142 ohm-cm

Descriptive Properties	Value	Comments
Deep-Drawing Capability rm	1.3	.0275 - .035 inches sheet thickness
Strain Hardening Exponent n	0.21	.0275 - .035 inches sheet thickness