Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Multibase Multi-Pro® 2005 RC I High Impact 20% Glass Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Multibase
Trade Name Multi-Pro®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase Multi-Pro® 2005 RC I High Impact 20% Glass Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Multi-Pro 2005 RC I is a chemically coupled polypropylene compound with increased stiffness, flex strength and excellent impact resistance. This product is geared for top engineering plastics applications in the automotive industry.Data provided by Multibase.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ASTM D792-91
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
ASTM D955-89
Melt Flow 5.0 g/10 min
5.0 g/10 min
(Condition L) ASTM D-1238-94a
Mechanical Properties Metric English Comments
Hardness, Shore D 77
77
10 sec; ASTM D-2240-95
Tensile Strength, Ultimate 58.6 MPa
8500 psi
ASTM D638-95
Elongation at Break 5.0 %
5.0 %
ASTM D638-95
Flexural Modulus 3.103 GPa
450.1 ksi
Method 1, Proc. B; ASTM D-790-95
Izod Impact, Notched 0.960 J/cm
1.80 ft-lb/in
ASTM D256-93a
Gardner Impact 0.400 J
0.295 ft-lb
ASTM D5420-93
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 138 °C
280 °F
ASTM D648-95
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
ASTM D648-95