Multibase Multi-Flex® D 2010 TPE Thermoplastic Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Multibase |
| Trade Name | Multi-Flex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Flex® D 2010 TPE Thermoplastic Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Chemical Resistance, Good Colorability, GoodElasticity, HighElectrically InsulatingFlame RetardantFlexibility, GoodHeat StabilizedOzone ResistantProcessability, GoodUV Resistance, Good Forms:PelletsProcessing Method:Injection Molding Information provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.88 g/cc | 1.88 g/cc | ASTM 792 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 77 | 77 | 10 seconds; ASTM D2240 |
| Tensile Strength, Yield | 2.76 MPa | 400 psi | Elastic; ASTM D412 |
| Elongation at Break | 500 % | 500 % | Elastic; ASTM D412 |
| Flexural Modulus | 0.0276 GPa | 4.00 ksi | ASTM D790 |
| Tear Strength | 21.0 kN/m | 120 pli | ASTM D624 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 210 °C | 410 °F | |
| Front Barrel Temperature | 227 °C | 440 °F | |
| Nozzle Temperature | 235 °C | 455 °F | |
| Mold Temperature | 51.7 °C | 125 °F | |
| Drying Temperature | 51.7 °C | 125 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 3.45 - 4.83 MPa | 500 - 700 psi | |
| Back Pressure | 0.345 MPa | 50.0 psi | |
| Screw Speed | 40 rpm | 40 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clamp Tonnage | 1.5-2.5 tons/in2 | |
| Injection Rate | Fast | |
| Suggested Max Regrind | 0.5 |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 1508 M Polypropylene
- SABIC Innovative Plastics Cycoloy® C2950 PC+ABS
- PSM Industries Pacific Sintered Metals Infiltrated Iron FX-226-T Powdered Metal
- Inno-Comp INNOPOL® CS 2-3000 Polypropylene Block-Copolymer
- SABIC Innovative Plastics Ultem 2200N PEI
- Saint-Gobain CHR® H7525 Glass-Silicone Backing Silicone Adhesive Pressure Sensitive Tape
- Schott N-LAK8 Glass
- A. Schulman SCHULAMID® 66 GF33HS 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- Colorite Polymers CS8042SC Wire and Cable Jacket Vinyl Compound
- Addcomp ADD-VANCE® FR 825 EVA based flame-retardant masterbatch