Multibase Multi-Flex® A 6202 MR TPE Thermoplastic Elastomer

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	Multibase
Trade Name	Multi-Flex®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Multibase Multi-Flex® A 6202 MR TPE Thermoplastic Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: Chemical Resistance, Good Colorability, GoodElasticity, HighElectrically InsulatingFlame RetardantFlexibility, GoodHeat StabilizedOzone ResistantProcessability, GoodUV Resistance, Good Scratch ResistantForms:PelletsProcessing Method:Extrusion Information provided by Multibase

Physical Properties	Metric	English	Comments
Specific Gravity	0.920 g/cc	0.920 g/cc	ASTM 792
Linear Mold Shrinkage	0.016 cm/cm	0.016 in/in	ASTM D955
Melt Flow	10 g/10 min @Load 2.16 kg, Temperature 230 °C	10 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	67	67	10 seconds; ASTM D2240
Tensile Strength, Yield	2.14 MPa	310 psi	at 100%; ASTM D412
	5.86 MPa	850 psi	Elastic; ASTM D412
Elongation at Break	700 %	700 %	Elastic; ASTM D412
Tear Strength	31.6 kN/m	180 pli	ASTM D624

Thermal Properties	Metric	English	Comments
Flame Spread	7.6 mm/min	0.30 in/min	VSS-302

Processing Properties	Metric	English
Middle Barrel Temperature	210 °C	410 °F
Front Barrel Temperature	227 °C	440 °F
Nozzle Temperature	235 °C	455 °F
Mold Temperature	51.7 °C	125 °F
Drying Temperature	51.7 °C	125 °F
Dry Time	2 - 4 hour	2 - 4 hour
Injection Pressure	3.45 - 4.83 MPa	500 - 700 psi
Back Pressure	0.345 MPa	50.0 psi
Screw Speed	40 rpm	40 rpm

Descriptive Properties	Value	Comments
Clamp Tonnage	1.5-2.5 tons/in²
Injection Rate	Fast
Suggested Max Regrind	0.5