Multibase Multi-ABS 3259 Plating Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Plating Grade |
| Manufacturer | Multibase |
| Trade Name | Multi-ABS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-ABS 3259 Plating Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Multibase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min | (Condition G) ASTM D-1238-94a |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 101 | 101 | ASTM D785-95 |
| Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM D638-95 |
| Elongation at Break | 40 % | 40 % | ASTM D638-95 |
| Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790-95 |
| Flexural Modulus | 2.255 GPa | 327.1 ksi | RT; ASTM D-790-95 |
| Izod Impact, Notched | 2.46 J/cm | 4.61 ft-lb/in | ASTM D256-93a |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | injection molded unannealed; ASTM D-648-95 |
| 203 °C | 397 °F | injection molded annealed; ASTM D-648-95 | |
| Vicat Softening Point | 95.0 °C | 203 °F | ASTM D1525-95 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
Users viewing this material also viewed the following:
- Pau Tai UNISTAB MS-550 Solid Complex Stabilizer
- A. Schulman POLYBATCH™ Gold 7060E POLYBATCH® Concentrate Based In LDPE
- BNZ Materials Blazecrete 3000 G Dense Castable
- Arkema Group Orgalloy® LE 60THM Flexible Nylon Alloy (Conditioned)
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 1.0 PHR Thanecure ZM
- LATI Latilon 28D G/30 PC, 30% Glass Fiber Reinforced
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 410, Hardened + 204°C Temper
- H.C. Starck Amperit® 552.072 Tungsten Carbide - Chromium Carbide-Nickel 73-20-7 (WC-CrC-Ni)
- Latrobe Nitralloy® 135 Modified VAC-ARC, 1.5 to 3 in Premium Nitriding Steel
Copyright © lookpolymers.com All Rights Reserved