Samyang Tribit® 1500G20 PBT, Reinforced General Purpose
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | Samyang |
| Trade Name | Tribit® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Tribit® 1500G20 PBT, Reinforced General Purpose.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Crystallization is fast, formability is excellent and thermal resistance, chemical resistance, electrical properties and abrasion resistance are excellent.1500G20 is a reinforced, general purpose grade.Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Water Absorption | 0.080 % | 0.080 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.012 cm/cm | 0.0020 - 0.012 in/in | ASTM D955 |
| Melt Flow | 50 g/10 min @Load 2.16 kg, Temperature 250 °C |
50 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength | 108 MPa | 15600 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 147 MPa | 21300 psi | ASTM D790 |
| Flexural Modulus | 4.41 GPa | 640 ksi | ASTM D790 |
| Izod Impact, Notched | 0.588 J/cm @Thickness 3.17 mm |
1.10 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.2 | 3.2 | ASTM D150 |
| Dielectric Strength | 21.0 kV/mm | 533 kV/in | ASTM D149 |
| Dissipation Factor | 0.020 | 0.020 | ASTM D150 |
| Arc Resistance | 150 sec | 150 sec | ASTM D495 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® SLX2431D PC Copolymer (Asia Pacific)
- MV Labs ZN1000 ZnSO4·7H2O Zinc sulfate heptahydrate
- SABIC Innovative Plastics Xenoy® 1101 PBT+PC (Asia Pacific)
- Saint-Gobain COHRlastic® 3016 Low Temperature Flexibility Silicone Coated Fabric
- ExxonMobil Exceed™ 1018MK Metallocene Polyethylene Resin
- Clariant Renol PA123G13 Nylon 66, 13% Glass Fiber, Impact Modified, Heat Stabilized, Lubricated
- Dow Corning 290 PAINTABLE RELEASE AGENT
Copyright © lookpolymers.com All Rights Reserved