- Multibase Multi-ABS 3075 High Impact
Multibase Multi-ABS 3075 High Impact
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Multibase |
| Trade Name | Multi-ABS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-ABS 3075 High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Multibase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792-91 |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | (Condition L) ASTM D-1238-94a |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785-95 |
| Tensile Strength, Ultimate | 37.2 MPa | 5400 psi | ASTM D638-95 |
| Elongation at Break | 25 % | 25 % | ASTM D638-95 |
| Flexural Strength | 53.8 MPa | 7800 psi | ASTM D790-95 |
| Flexural Modulus | 2.00 GPa | 290 ksi | RT; ASTM D-790-95 |
| Izod Impact, Notched | 4.00 J/cm | 7.49 ft-lb/in | ASTM D256-93a |
| Gardner Impact | 10.6 J | 7.82 ft-lb | ASTM D5420-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | injection molded annealed; ASTM D-648-95 |
| Vicat Softening Point | 107 °C | 225 °F | ASTM D1525-95 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 35.4 kV/mm | 899 kV/in | ASTM D149-95 |
Users viewing this material also viewed the following:
- Parker Chomerics SOFT-SHIELD® 4002 Low Closure Force, Foam Core EMI Gasket
- LyondellBasell Pro-fax SB891 Polypropylene Impact Copolymer
- Kobe Steel KS100 Commercially Pure Titanium, Annealed
- Michelman® Michem® Emulsion 47950 Nonionic paraffin emulsion
- Styron XZ 92092.00 Carboxylated SB
- ChevronTexaco Clarity® ISO 460 Paper Machine Oil
- A. Schulman ComAlloy Hiloy® 518 Polycarbonate, Carbon Fiber Reinforced
- ALM PA 620-MF Mineral Fiber Filled Nylon 12 SLS Prototyping Polymer
- DuPont Performance Polymers Hypalon® 30 Chlorosulfonated Polyethylene Rubber, Carbon Black Filled Compound (d
Copyright © lookpolymers.com All Rights Reserved