Momentive Performance Materials RTV157 High Strength Silicone Adhesive Sealant, Gray

Category Polymer , Adhesive , Thermoset , Silicone , Silicone, RTV, Adhesive/Sealant Grade
Manufacturer Momentive Performance Materials (Former GE Silicones)
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Momentive Performance Materials RTV157 High Strength Silicone Adhesive Sealant, Gray.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
RTV 157 is a one component, ready-to-use, high strength silicone rubber adhesive sealant. It cures to tough resilient silicone rubber on exposure to atmospheric moisture at room temperature. RTV157 releases acetic acid as a by-product of cure.RTV157 sealant is a paste consistency product which can be applied to horizontal, vertical, and overhead surfaces in applications requiring high strength and temperature performance.Since this adhesive sealants utilizes a moisture cure system, it must not be used in thicknesses greater than 6mm(1/4in.). Where section depths exceed 6mm (1/4 in.), GE Silicones one-component, addition cure or two-component silicone rubber compounds are suggested.This sealant was not designed for and should not be used for applications intended for permanent implantation into the human body.Mechanical properties for specimen cured 3 days at 25°C and 50% relative humidity.Key Performance Properties: High strengthHigh temperature performanceLow temperature flexibilityOne-componentRoom temperature cureGeneral primerless adhesionExcellent electrical insulation propertiesExcellent weatherability, ozone, and chemical resistanceGE Silicones became a part of Momentive Performance Materials in 2006.
Physical Properties Metric English Comments
Specific Gravity 1.09 g/cc
1.09 g/cc
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
Mechanical Properties Metric English Comments
Hardness, Shore A 28
28
Tensile Strength, Ultimate 6.73 MPa
976 psi
Cured 7 days at 25°C and 50% relative humidity
Elongation at Break 825 %
825 %
Tear Strength 16.7 kN/m
95.2 pli
Peel Strength 10.5 kN/m
60.0 pli
Cured 7 days at 25°C and 50% relative humidity
Thermal Properties Metric English Comments
CTE, linear 270 µm/m-°C

@Temperature 20.0 °C
150 µin/in-°F

@Temperature 68.0 °F
Thermal Conductivity 0.209 W/m-K
1.45 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air 204 °C
399 °F
Continuous
260 °C
500 °F
Intermittent
Brittleness Temperature -60.0 °C
-76.0 °F
Electrical Properties Metric English Comments
Volume Resistivity 7.50e+14 ohm-cm
7.50e+14 ohm-cm
Dielectric Constant 2.9
2.9
Dielectric Strength 20.7 kV/mm
526 kV/in
Dissipation Factor 0.00090
0.00090
Processing Properties Metric English Comments
Cure Time 45.0 min
0.750 hour
Tack-free
Descriptive Properties Value Comments
Application rate 155 g/min
Color Gray
Consistency Paste