Category | Polymer , Thermoplastic , Nylon |
Manufacturer | Mitsui Chemicals America |
Trade Name | Arlen™ |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Mitsui Arlen™ C215 15% Glass Fiber-Reinforced Modified Nylon 6T (DAM).pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
Filler Content | 15 % | 15 % | |
Water Absorption | 0.4 % @Thickness 2.00 mm |
0.4 % @Thickness 0.0787 in |
24 hours in 23°C water; ASTM D570 |
3.8 % @Thickness 2.00 mm |
3.8 % @Thickness 0.0787 in |
24 hours in 100°C water; ASTM D570 | |
Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 2.00 mm |
0.0060 in/in @Thickness 0.0787 in |
ASTM D955 |
Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm |
0.0090 in/in @Thickness 0.0787 in |
Vertical Direction; ASTM D955 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Rockwell M | 105 | 105 | ASTM D785 |
Tensile Strength at Break | 110 MPa | 16000 psi | ASTM D638 |
Elongation at Break | 3.0 % | 3.0 % | Measured between the chucks; ASTM D638 |
Flexural Strength | 180 MPa | 26100 psi | ASTM D790 |
Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D790 |
Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 55.0 µm/m-°C @Temperature 20.0 °C |
30.6 µin/in-°F @Temperature 68.0 °F |
Vertical Direction; ASTM D696 |
CTE, linear, Parallel to Flow | 34.0 µm/m-°C @Temperature 20.0 °C |
18.9 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Melting Point | 310 °C | 590 °F | |
Deflection Temperature at 1.8 MPa (264 psi) | 295 °C | 563 °F | ASTM D648 |
Glass Transition Temp, Tg | 85.0 °C | 185 °F | |
Flammability, UL94 | HB | HB |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
Dielectric Constant | 4.2 @Frequency 1e+6 Hz |
4.2 @Frequency 1e+6 Hz |
ASTM D150 |
Dielectric Strength | 25.0 kV/mm | 635 kV/in | ASTM D149 |
Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
ASTM D150 |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Feed Temperature | 50.0 - 90.0 °C | 122 - 194 °F | Hopper Bottom for Electronic and Electric Standard Molding |
50.0 - 90.0 °C | 122 - 194 °F | Hopper Bottom Temp for Mechanical and Structural Standard Molding | |
Nozzle Temperature | 315 - 335 °C | 599 - 635 °F | NH Cylinder Temp for Electronic and Electric Standard Molding |
325 - 340 °C | 617 - 644 °F | NH Cylinder Temp for Mechanical and Structural Standard Molding | |
Zone 1 | 300 - 325 °C | 572 - 617 °F | C1 Cylinder Temp for Electronic and Electric Standard Molding |
315 - 330 °C | 599 - 626 °F | C1 Cylinder Temp for Mechanical and Structural Standard Molding | |
Zone 2 | 315 - 335 °C | 599 - 635 °F | C2 Cylinder Temp for Electronic and Electric Standard Molding |
320 - 335 °C | 608 - 635 °F | C2 Cylinder Temp for Mechanical and Structural Standard Molding | |
Zone 3 | 320 - 335 °C | 608 - 635 °F | C3 Cylinder Temp for Electronic and Electric Standard Molding |
325 - 340 °C | 617 - 644 °F | C3 Cylinder Temp for Mechanical and Structural Standard Molding | |
Mold Temperature | 90.0 - 140 °C | 194 - 284 °F | for Electronic and Electric Standard Molding |
90.0 - 140 °C | 194 - 284 °F | for Mechanical and Structural Standard Molding | |
Screw Speed | 150 rpm | 150 rpm | for Mechanical and Structural Standard Molding |
150 rpm | 150 rpm | for Electronic and Electric Standard Molding |
Descriptive Properties | Value | Comments |
---|---|---|
Injection Pressure | Medium | Electronic and Electric Standard Molding |
Medium | Mechanical and Structural Standard Molding | |
Injection Speed | Medium | Electronic and Electric Standard Molding |
Medium | Mechanical and Structural Standard Molding |