Mitsui APELâ„¢ APL6015T Cyclo Olefin Copolymer (COC)
| Category | Polymer , Thermoplastic , Cyclo Olefin Polymer |
| Manufacturer | Mitsui Chemicals America |
| Trade Name | APEL™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Mitsui APELâ„¢ APL6015T Cyclo Olefin Copolymer (COC).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This material possesses many characteristics inherent in polyolefins such as excellent electrical insulating properties and outstanding moisture resistance. In addition, it features good melt processability/flowability, good clarity and transparency, high glass transition temperature (Tg), exceptional moisture impermeability, impressive gas barrier qualities and excellent chemical and heat resistance. This material is used in Medical Package applications.Information provided by Mitsui Chemicals America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Moisture Vapor Transmission | 0.0900 cc-mm/m²-24hr-atm | 0.229 cc-mil/100 in²-24hr-atm | 1 atm; ASTM D1249 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | MCI Method |
| Melt Index of Compound | 10 g/10 min @Load 2.16 kg, Temperature 260 °C |
10 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ASTM D790 |
| Izod Impact, Notched | 0.250 J/cm | 0.468 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 155 °C | 311 °F | TMA; MCI Method |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
| Glass Transition Temp, Tg | 145 °C | 293 °F | MCI Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.54 | 1.54 | ASTM D542 |
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Transmission, Visible | 90 % | 90 % | ASTM D1003 |
Users viewing this material also viewed the following:
- PlastiComp Complet® LCF40 - PA66 MT Nylon 66, 40% Long Carbon Fiber Reinforced, Impact Modified
- Loxim 230 12HB Polybutylene Terephthalate
- Techmer ES Luriblend® PBT GB30 TL15 30% Glass Bead Filled
- Struktol POLYDIS 3622 Elastomer modified epoxy prepolymer
- Saint-Gobain Norton® Log Home Foam® V790
- Teknor Apex Sarlink® 4155 Thermoplastic Elastomer
- UCAR Carbon UCAR® CSX Extruded Graphite
- Asahi Glass AFLAS® 150CS TFE/P Fluoroelastomer
- Ascend Performance Materials Vydyne® R533H NAT Nylon 66, 33% Glass Reinforced, Conditioned
- Schmolz + Bickenbach Holder Block Plastic Mold Steel
Copyright © lookpolymers.com All Rights Reserved