Mitsubishi Iupital® F10-02 High Viscosity Acetal Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Mitsubishi |
| Trade Name | Iupital® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Mitsubishi Iupital® F10-02 High Viscosity Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Water Absorption | 0.22 % | 0.22 % | 24 Hr.; ASTM D570 |
| Linear Mold Shrinkage | 0.022 cm/cm | 0.022 in/in | ASTM D955 |
| Melt Flow | 2.5 g/10 min | 2.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 78 | 78 | ASTM D785 |
| Tensile Strength, Yield | 60.3 MPa @Thickness 3.17 mm |
8750 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 65 % @Thickness 3.17 mm |
65 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Strength | 88.3 MPa @Thickness 3.17 mm |
12800 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 2.57 GPa @Thickness 3.17 mm |
373 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 0.742 J/cm @Thickness 3.17 mm |
1.39 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
Users viewing this material also viewed the following:
- PolyOne LubriOne™ PS-30GF/2S Natural Polybutylene Terephthalate (PBT)
- Petroquimica Triunfo Trithene® TS 7001 LDPE - Heavy Duty Low Friction Film
- Solvay Engineered Polymers SEQUEL® 1820 Engineered Polyolefin (discontinued **)
- ExxonMobil ESCOR™ AT 320 Cast Film Resin (discontinued **)
- Mallard Creek Polymers Rovene® 4045 Styrene-Butadiene Emulsion
- Saint-Gobain CHR® SG13-10(R) High Performance Glass-PTFE Backing Acrylic Adhesive Pressure Sensitive Tape
- SABIC Innovative Plastics Noryl GTX GTX966 PPE+PA66
- Supreme Petrochem SP 6456 High Heat Polystyrene
- 3M Dyneon™ TF 2021Z PTFE Fine Powder
Copyright © lookpolymers.com All Rights Reserved