Supreme Petrochem SP 562 Flame Retardant Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Flame Retardant |
| Manufacturer | Supreme Petrochem LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Supreme Petrochem SP 562 Flame Retardant Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics Very good flow properties Free of DBDPO, PBDE & TBBA, complies with ROHS directive of EU Low specific gravity Processing Injection moldingApplications Large size T.V. Cabinets Audio cabinets Electrical boxes, electrical appliance parts Electrical distribution components, fuse carriers, enclosures etc.Material Status: Commercial : ActiveAgency Ratings: Information provided by Supreme Petrochem LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 28.4 MPa | 4120 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ASTM D638 |
| Flexural Strength | 37.3 MPa @Thickness 3.20 mm |
5410 psi @Thickness 0.126 in |
ASTM D790 |
| Flexural Modulus | 2.06 GPa @Thickness 3.20 mm |
299 ksi @Thickness 0.126 in |
ASTM D790 |
| Izod Impact, Notched | 1.10 J/cm @Thickness 3.20 mm |
2.06 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 78.0 °C | 172 °F | IEC335-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | ASTM D648 |
| Vicat Softening Point | 97.0 °C | 207 °F | 1kg / 120°C; ASTM D1525 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 93 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 93 |
| Dielectric Constant | 2.6 @Frequency 1e+6 Hz |
2.6 @Frequency 1e+6 Hz |
IEC 250 |
| Dissipation Factor | 0.00040 @Frequency 1e+6 Hz |
0.00040 @Frequency 1e+6 Hz |
IEC 250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | <= 250 °C | <= 482 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 60.0 - 80.0 °C | 140 - 176 °F | ( 2 hrs) Pre drying temp. |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable JKC30A Polyvinyl Chloride, Flexible (PVC, Flexible)
- Polymer Resources PC-FR-IM1 Polycarbonate, Preliminary Data Sheet, Low Temperature Impact and Flame Retardant
- Techmer ES Luriblend® PA6/6 TL20 Nylon 66
- Silon Taborex TA 2120 HD Catalyst Masterbatch
- A. Schulman POLYFORT™ FPP 3460 Glass-Mineral Hybrid Filled Copolymer
- CIMBAR CIMBAR™ PC Barite Powder (BaSO4)
- ConocoPhillips Hydroclear® 68 Multi-Way Machine Lubricant
- BASF Octamethylenediamine
- 3A Composites Core Materials AIREX® T90.100 Easy Processing Structural FST Foam
- Overview of materials for Polyethylene Terephthalate (PET), 20% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved