SABIC Innovative Plastics ULTEM ATX3562R PEI+PCE (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI) + PCE |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM ATX3562R PEI+PCE (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
50% Glass fiber and mineral filled, high flow Polyetherimide blend with internal mold release and enhanced dimensional stability. RoHS compliant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.69 g/cc | 1.69 g/cc | ASTM D792 |
| Density | 1.69 g/cc | 0.0611 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0400 % | 0.0400 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.10 % | 0.10 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 20 g/10 min @Load 6.60 kg, Temperature 337 °C |
20 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 360 °C |
20 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 121 MPa | 17500 psi | 5 mm/min; ISO 527 |
| 125 MPa | 18100 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 121 MPa | 17500 psi | 5 mm/min; ISO 527 |
| 125 MPa | 18100 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 14.69 GPa | 2131 ksi | 1 mm/min; ISO 527 |
| 14.94 GPa | 2167 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 172 MPa | 24900 psi | 2 mm/min; ISO 178 |
| 180 MPa | 26100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 12.9 GPa | 1870 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 13.55 GPa | 1965 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
| 0.490 J/cm @Temperature -30.0 °C |
0.918 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 1.11 J/cm @Thickness 3.20 mm |
2.08 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1U |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 12.0 J @Temperature 23.0 °C |
8.85 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.0 µm/m-°C @Temperature -40.0 - 150 °C |
8.89 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 16.0 µm/m-°C @Temperature 23.0 - 150 °C |
8.89 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 38.0 µm/m-°C @Temperature -40.0 - 150 °C |
21.1 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 38.0 µm/m-°C @Temperature 23.0 - 150 °C |
21.1 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 182 °C | 360 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 183 °C @Thickness 3.20 mm |
361 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 184 °C | 363 °F | Rate B/50; ASTM D1525 |
| 187 °C | 369 °F | Rate B/50; ISO 306 | |
| 195 °C | 383 °F | Rate B/120; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 6.00e+15 ohm-cm | 6.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 2.10e+15 ohm | 2.10e+15 ohm | ASTM D257 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | Passes | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering N70J Nitrile Rubber
- Polykemi AB POLYfill PPC K20010 PP, 10% Mineral Reinforced
- Lehmann & Voss LUVOCOM® 1301-7178 PPS, linear, with glass fiber
- Lubriplate 730-2 Aluminum Complex Multi-Purpose Grease
- SABIC Innovative Plastics LNP Stat-kon FX99030 PE (Europe-Africa-Middle East)
- SABIC Innovative Plastics ULTEM AUT230 PEI (Asia Pacific)
- Wieland 1608 Wilaform Gold
- Ashley Polymers Ashlene® 990L Nylon 610
- Zircar Zirconia ZYBF-5 Zirconia Bulk Fiber Insulation
- Colorite Polymers 8000 General Purpose Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved