Master Bond Super Gel 9 Two component urethane modified epoxy gel-like system

Category Polymer , Thermoset , Epoxy
Manufacturer Master Bond Inc.
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Master Bond Super Gel 9 Two component urethane modified epoxy gel-like system.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cures at room temperature to form a soft, resilient gel-like system with good dimensional stability. It has excellent optical clarity, convenient to handle, and is easy to retrieve with a sharp knife or blade.
Physical Properties Metric English Comments
Viscosity 75 - 150 cP

@Temperature 23.9 °C
75 - 150 cP

@Temperature 75.0 °F
Part B
7000 - 12000 cP

@Temperature 23.9 °C
7000 - 12000 cP

@Temperature 75.0 °F
Part A
Mechanical Properties Metric English Comments
Hardness, Shore A <= 5
<= 5
Tensile Strength 2.76 MPa
400 psi
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 93.3 °C
200 °F
Minimum Service Temperature, Air -73.3 °C
-100 °F
Optical Properties Metric English Comments
Refractive Index 1.5253
1.5253
Electrical Properties Metric English Comments
Volume Resistivity >= 1e+15 ohm-cm
>= 1e+15 ohm-cm
Dielectric Constant 4.1

@Frequency 60.0 Hz
4.1

@Frequency 60.0 Hz
Dielectric Strength >= 16.5 kV/mm

@Thickness 3.17 mm
>= 420 kV/in

@Thickness 0.125 in
Dissipation Factor 0.090

@Frequency 60.0 Hz
0.090

@Frequency 60.0 Hz
Processing Properties Metric English Comments
Processing Temperature 23.9 °C

@Time 346000 - 605000 sec
75.0 °F

@Time 96.0 - 168 hour
may be accelerated to about 55 hours with heat
Pot Life 360 - 480 min

@Temperature 23.9 °C
360 - 480 min

@Temperature 75.0 °F
200 g batch
420 - 540 min

@Temperature 23.9 °C
420 - 540 min

@Temperature 75.0 °F
100 g batch
Shelf Life 12.0 Month
12.0 Month
unopened containers at RT
Descriptive Properties Value Comments
Mix Ratio, A:B 2:1
By weight or volume