Samsung Cheil Industries Starex® HF-0690M ABS, Unreinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® HF-0690M ABS, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Melt Flow | 8.9 g/10 min @Load 5.00 kg, Temperature 200 °C |
8.9 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 109 | 109 | ASTM D785 |
| Tensile Strength at Break | 32.4 MPa | 4700 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 39.2 MPa | 5690 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 20 % | 20 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.26 GPa | 327 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 62.8 MPa | 9110 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.35 GPa | 341 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.27 J/cm @Thickness 6.35 mm |
2.39 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 1.47 J/cm @Thickness 3.17 mm |
2.76 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C @Thickness 6.40 mm |
194 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C @Thickness 6.40 mm |
180 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 93.0 °C | 199 °F | B/50; ISO R306 |
| 95.0 °C | 203 °F | B/120; ISO R306 |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRESEAL 6080 Ag-Coated Glass
- Piezo Kinetics 409E Lead Zirconate Titanate Piezoelectric
- Shin-Etsu Silicones KF-8020 Fluid
- SABIC Innovative Plastics LNP STAT-KON FX98500 PE (Asia Pacific)
- A. Schulman POLYPUR™ FPU 1117 Thermoplastic Polyurethane Compound
- TSE Industries EzNATE® 200 Polyurethane Resin
- Borealis Xmod™ K65G2 20% Glass Fiber Reinforced Polypropylene Compound
- Epoxy Technology EPO-TEK® H20E-PFC Electrically Conductive, Silver Epoxy
- Advanced Polymer Alloys Alcryn® 1060 BK Melt Processable Rubber
- Fainplast Compounds KL 92 Flexible PVC, Insulation for High Temperatures Lead Free
Copyright © lookpolymers.com All Rights Reserved