Manifattura Cattaneo POM c Acetal
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Manifattura Cattaneo spa |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Manifattura Cattaneo POM c Acetal.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.20 % @Temperature 23.0 °C |
0.20 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 0.85 % | 0.85 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 84 | 84 | ISO 2039-2 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | ISO 527 |
| Elongation at Break | 33 % | 33 % | ISO 527 |
| Elongation at Yield | 10 % | 10 % | ISO 527 |
| Tensile Modulus | 2.80 GPa | 406 ksi | ISO 527 |
| Flexural Strength | 89.0 MPa | 12900 psi | |
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 |
| Compressive Yield Strength | 19.0 MPa @Strain 1.00 % |
2760 psi @Strain 1.00 % |
ISO 604 |
| Poissons Ratio | 0.43 | 0.43 | |
| Charpy Impact Unnotched | 28.0 J/cm² | 133 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 |
| Coefficient of Friction, Dynamic | 0.21 | 0.21 | on polished steel; MPC Test |
| Coefficient of Friction, Static | 0.14 | 0.14 | on polished steel; MPC Test |
| K Factor (Wear Factor) | 3.8 | 3.8 | µm/s. PV = 0.1 MPa-m/s; max P = 18 MPa; MPC Test |
| Limiting Pressure Velocity | 0.150 MPa-m/sec | 4280 psi-ft/min | without lubrication; MPC Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 110 µm/m-°C @Temperature 23.0 - 100 °C |
61.1 µin/in-°F @Temperature 73.4 - 212 °F |
ASTM D696 |
| Thermal Conductivity | 0.310 W/m-K | 2.15 BTU-in/hr-ft²-°F | DOM 52612 |
| Maximum Service Temperature, Air | 115 °C | 239 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ISO 75 |
| Flammability, UL94 | HB | HB | |
| V-2 | V-2 | ||
| Oxygen Index | 15 % | 15 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60094 |
| Dielectric Constant | 3.9 @Frequency 1.00e+6 Hz |
3.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 22.0 kV/mm @Thickness 2.00 mm |
559 kV/in @Thickness 0.0787 in |
IEC 60243 |
| Dielectric Loss Index | 0.0070 @Frequency 1.00e+6 Hz |
0.0070 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| FDA | Yes | Yes |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| White | ||
| UV Resistance | N |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPC GF15030 PD2 Polypropylene Copolymer, Glass Fiber Reinforced, Chemically Coupled
- Materion Nibryl Beryllium Nickel Alloy (Nibryl)-360 Rod and Bar; H925 (H925) Temper; All Sizes (UNS N03360)
- A. Schulman POLYFORT™ FPP 1605 Glass Reinforced Chemically Coupled Copolymer
- Alcoa Deltalloy® 4032-T86 Aluminum
- DSM Somos® ProtoGen™ 18920 Liquid Photopolymer, UV Postcure at HOC +3
- Eurostar Staramide PK005EI2 PA6, Mineral Fiber Filled, Impact Modified Injection Molded
- BNZ Materials BNZP-25L Insulating Firebrick (French Grade)
- Polyram Polytron A40B02 Nylon 66, 40% Long Fiber
Copyright © lookpolymers.com All Rights Reserved