- Techmer ES HiFill® PES GM20 WT139 20% Milled Glass Filled
Techmer ES HiFill® PES GM20 WT139 20% Milled Glass Filled
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 20%Glass Fiber Filled |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PES GM20 WT139 20% Milled Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Milled Glass Fiber, 20% Filler by WeightInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ASTM D792 |
| Water Absorption | 0.40 % @Time 86400 sec |
0.40 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 3.17 mm |
0.0020 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 98 | 98 | ASTM D785 |
| Tensile Strength, Yield | 133 MPa | 19300 psi | ASTM D638 |
| Elongation at Break | 2.9 % | 2.9 % | ASTM D638 |
| Flexural Strength | 186 MPa | 27000 psi | ASTM D790 |
| Flexural Modulus | 5.52 GPa | 800 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm @Thickness 3.17 mm |
1.40 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 32.4 µm/m-°C | 18.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable WJKC505L Polyvinyl Chloride, Flexible (PVC, Flexible)
- Polikim POLITAL® Polyoxymethylene (POM)
- Park Electrochemical Nelcote® P-600 Polyester Prepreg, 7781 E-Glass Reinforced
- Solvay Specialty Polymers Amodel® A-1340 HS Polyphthalamide (PPA) Resin, 40% Mineral/Glass Reinforced, at 50% RH &n
- A. Schulman PAPERMATCH® T-4228-8 Specialty Masterbatch
- ChevronTexaco Texmar ZF 17 SAE 40
- 3M Scotchkote™ EG 515 Urethane Ceramic Rebuild
- 3M Scotchcal™ ElectroCut™ 7725-23 Graphic Film
- Beijing Chemical Industry KAIFA® 301-G15F PBT Resin
Copyright © lookpolymers.com All Rights Reserved