LyondellBasell Moplen HP400H Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Extrusion Grade |
| Manufacturer | LyondellBasell |
| Trade Name | Moplen |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Moplen HP400H Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Moplen HP400H is a homopolymer for extrusion applications. Moplen HP400H exhibits easy processability and a good stiffness/impact balance at ambient temperature. The main applications of Moplen HP400H are thermoformed tubs and containers, medium draw trays and blister packs, flowerpots and small extrusion blow molded bottles. Moplen HP400H is suitable for food contact. Uses: Thermoformed containers, bottlesInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ASTM D792 & ISO 1183 |
| Water Absorption | 0.010 % | 0.010 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.015 - 0.018 cm/cm | 0.015 - 0.018 in/in | ASTM D955 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| 2.2 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.2 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 89 | 89 | ASTM D 785 |
| Ball Indentation Hardness | 70.0 MPa | 10200 psi | H 358/30; ISO 2039-1 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ISO 527-1, -2 |
| 34.6 MPa | 5020 psi | ASTM D 638 | |
| Elongation at Break | 50 % | 50 % | ISO 527-1, -2 |
| Elongation at Yield | 11 % | 11 % | ASTM D 638 & ISO 527-1, -2 |
| Tensile Modulus | 1.40 GPa | 203 ksi | ISO 527-1, -2 |
| Flexural Modulus | 1.37 GPa | 198 ksi | ASTM D790 |
| Izod Impact, Notched | 0.443 J/cm | 0.830 ft-lb/in | 73°F; ASTM D256 |
| Charpy Impact Unnotched | NB | NB | Type 1, Edgewise; ISO 179 |
| 9.00 J/cm² @Temperature 0.000 °C |
42.8 ft-lb/in² @Temperature 32.0 °F |
Type 1, Edgewise; ISO 179 | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | Type 1, Edgewise, Notch A; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 µm/m-°C @Temperature 100 °C |
55.6 µin/in-°F @Temperature 212 °F |
ASTM D696 |
| Specific Heat Capacity | 1.70 J/g-°C | 0.406 BTU/lb-°F | ASTM C351 |
| Thermal Conductivity | 0.202 W/m-K | 1.40 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | Unannealed; ISO 75B-1, -2 |
| 85.0 °C | 185 °F | Unannealed; ASTM D648 | |
| Vicat Softening Point | 80.0 °C | 176 °F | (B50 (50°C/h 50 N)); ISO 306 |
| 150 °C | 302 °F | (A50 (50°C/h 10 N)); ISO 306 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 241R PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP THERMOCOMP QF004 PA 6/10
- Tipco Tipcolene® FPZ-GC - Talc/Mineral Reinforced Polypropylene Copolymer, High Flow, Stiffness & Impact Strength
- A. Schulman CP775-01 Molding Grade, Low Density Polyethylene
- Eastman Tenite 360E4861316 Cellulose Acetate Propionate, Clear, Trsp
- DuPont Performance Polymers Crastin® SK692FR NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)&l
- LATI Latilub 95-25GR CE/10 PSU, Mineral Fiber Reinforced, Graphite Filled
- SABIC Innovative Plastics Lexan® 945 PC (Asia Pacific)
- BIW ASTM Class 2D4 Silicone Foam
Copyright © lookpolymers.com All Rights Reserved