LyondellBasell Hifaxâ„¢ AA36H Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifaxâ„¢ AA36H Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hifaxâ„¢ AA36H conventional melt flow, 1,400 MPa flexural modulus, UL 94 V-2 flame retardant polypropylene homopolymer resin has an excellent combination of properties and processability. It was designed for applications that require flame and heat resistance, along with good electrical properties and surface quality. Uses: Appliances, electrical parts, household goodsInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM D955 |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 96 | 96 | ASTM D 785 |
| Tensile Strength at Break | 29.6 MPa | 4300 psi | ASTM D 638 |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D 638 |
| Elongation at Break | 200 % | 200 % | ASTM D 638 |
| Flexural Modulus | 1.40 GPa | 203 ksi | 1% Secant, 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | 73°F; ASTM D256 |
| Gardner Impact | 3.01 J @Temperature -30.0 °C |
2.22 ft-lb @Temperature -22.0 °F |
ASTM D3029, tested in accordance with ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | Unannealed; ASTM D648 |
| UL RTI, Electrical | 115 °C | 239 °F | 0.118 in; UL 746 |
| UL RTI, Mechanical with Impact | 115 °C | 239 °F | 0.118 in; UL 746 |
| UL RTI, Mechanical without Impact | 115 °C | 239 °F | 0.118 in; UL 746 |
| Flammability, UL94 | V-2 | V-2 | 0.0591 in |
| Oxygen Index | 26 % | 26 % | ASTM D2863 |
| Shrinkage | 1.6 % | 1.6 % | Tool, 100x150x3.2 mm Injection Molded Plaque; Basell Test Method |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 7.60e+16 ohm-cm | 7.60e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 42.9 kV/mm | 1090 kV/in | ASTM D149 |
| Arc Resistance | 88 sec | 88 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Radici Radilon® S 32HS (dry) Nylon 6
- Solvay Specialty Polymers Ryton® R-4 Polyphenylene Sulfide Compound (Unverified Data**)
- Kennametal Stellite Stellite® 12 PM with P/M Processing
- Techmer ES HiFill® PBT G/CF30 40% Glass Bead Filler
- SABIC Innovative Plastics LNP Thermocomp PH0600A PA 6
- DuPont Elvaloy® HP661 Ethylene/N-Butyl Acrylate/Carbon Monoxide Copolymer
- A. Schulman ComAlloy Comtuf® 639 Nylon 6/6, Mineral Reinforced, Impact Modified, Flow Enhanced
- Arlon 47571R007 0.007" (0.178 mm) Uncured Silicone Rubber with Fiberglass Substrate
- A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved