LyondellBasell Alathon® H6017 High Density Polyethylene, Injection Molding Grade
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded |
| Manufacturer | LyondellBasell (former Equistar) |
| Trade Name | Alathon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Alathon® H6017 High Density Polyethylene, Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ALATHON H6017 provides good processing characteristics and exhibits excellent toughness and color as well as low odor and good molded-part stability. Typical applications include housewares, caps, closures and various food containers.Regulatory Status: H6017 meets the requirements of the Food and Drug Administration regulation 21 CFR 177.1520. This regulation allows the use of this olefin polymer in "...articles or components of articles intended for use in contact with food." Specific limitations or conditions of use may apply. Contact your Equistar sales representative for more information.Specific recommendations for processing H6017 can only be made when the processing conditions, equipment and end use application are known.This product is from the former Equistar product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.593 - 0.625 g/cc | 0.0214 - 0.0226 lb/in³ | ASTM D1895 |
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D1505 |
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 190 °C |
18 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Spiral Flow | 28.2 cm | 11.1 in | Equistar test |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 72 | 72 | ASTM D2240 |
| Tensile Strength at Break | 29.6 MPa | 4300 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 12 % | 12 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 0.8680 GPa | 125.9 ksi | 1% Secant; 50mm/min; ASTM D638 |
| 1.001 GPa | 145.2 ksi | 50mm/min; ASTM D638 | |
| Flexural Modulus | 1.118 GPa | 162.2 ksi | 2% Secant; 12.5 mm/min; ASTM D790 |
| 1.369 GPa | 198.5 ksi | 1% Secant; 12.5 mm/min; ASTM D790 | |
| 1.474 GPa | 213.8 ksi | 12.5 mm/min; ASTM D790 | |
| Izod Impact, Notched | 0.395 J/cm | 0.740 ft-lb/in | ASTM D256 |
| 5.34 J/cm @Temperature -18.0 °C |
10.0 ft-lb/in @Temperature -0.400 °F |
ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 133.0 °C | 271.4 °F | ASTM D3418 |
| Crystallization Temperature | 115.7 °C | 240.3 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Vicat Softening Point | 128 °C | 262 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 232 °C | 450 °F | |
| Middle Barrel Temperature | 243 °C | 470 °F | |
| Front Barrel Temperature | 246 °C | 475 °F | |
| Nozzle Temperature | 246 °C | 475 °F |
Users viewing this material also viewed the following:
- Mitsubishi Hostaphan® RN, 50 micron Nominal Thickness Universal Polyethylene Terephthalate Film
- Haynes Hastelloy® C-2000® Nickel Alloy Shielded Metal Arc Welded (SMAW) All Weld Cruciform
- Styrolution Terblend® N NM-21 EF Gray 38058 ABS+PA (Conditioned)
- SCG Chemicals EL-Leneâ„¢ M40 Butene (C4) Rotational Molding Resin
- American Elements Niobium Nanoparticles
- ChevronTexaco 22 White Oil
- Denka VINYKON S3097 PVC, S grade for refrigerator gaskets
- BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Dry)
- Gromax PBT 3015-104 15% Glass Fiber Filled
- DuPont Performance Polymers VTR 8505/8500 Formulation (discontinued **)
Copyright © lookpolymers.com All Rights Reserved