SABIC Innovative Plastics LNP THERMOCOMP OF008H PPS - Linear

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP OF008H PPS - Linear.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* OF008H is a compound based on PPS - Linear containing 40% Glass Fiber. Characteristics of this grade are: Healthcare.
Physical Properties Metric English Comments
Density 1.70 g/cc
0.0614 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0030 cm/cm

@Time 86400 sec
 0.0030 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.010 cm/cm

@Time 86400 sec
 0.010 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 1.6 %
1.6 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 14.1 GPa
2050 ksi
50 mm/min; ASTM D638
Flexural Strength 234 MPa
33900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 14.22 GPa
2062 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.960 J/cm
1.80 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.34 J/cm
10.0 ft-lb/in
ASTM D4812
Coefficient of Friction, Dynamic 0.41
0.41
ASTM D3702 Modified
Coefficient of Friction, Static 0.50
0.50
ASTM D3702 Modified
K (wear) Factor 751 x 10-8 mm³/N-M
373 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 264 °C

@Thickness 3.20 mm
 507 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 0.450 mm
 V-0

@Thickness 0.0177 in
 UL 94 by SABIC-IP