DuPont Performance Polymers Delrin® 500AL NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 500AL NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lubricated Medium Viscosity Acetal Homopolymer with Low Wear and Low Friction Delrin 500AL is a medium viscosity acetal homopolymer with an advanced system of lubrication for applications requiring low wear and/or coefficient of friction against steelInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.018 cm/cm
0.018 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.017 cm/cm
0.017 in/in
ISO 294-4 2577
Melt Flow 12 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 12 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm³/10min; ISO 1133
14 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 14 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Stress 16.3 MPa

@Strain 0.500 %,
Temperature 23.0 °C
 2360 psi

@Strain 0.500 %,
Temperature 73.4 °F
 ISO 11403-1 -2
18.7 MPa

@Strain 0.500 %,
Temperature -40.0 °C
 2710 psi

@Strain 0.500 %,
Temperature -40.0 °F
 ISO 11403-1 -2
47.7 MPa

@Strain 2.00 %,
Temperature 23.0 °C
 6920 psi

@Strain 2.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
59.2 MPa

@Strain 3.50 %,
Temperature 23.0 °C
 8590 psi

@Strain 3.50 %,
Temperature 73.4 °F
 ISO 11403-1 -2
62.8 MPa

@Strain 2.30 %,
Temperature -40.0 °C
 9110 psi

@Strain 2.30 %,
Temperature -40.0 °F
 ISO 11403-1 -2
63.6 MPa

@Strain 5.00 %,
Temperature 23.0 °C
 9220 psi

@Strain 5.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
84.1 MPa

@Strain 4.00 %,
Temperature -40.0 °C
 12200 psi

@Strain 4.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
91.4 MPa

@Strain 6.00 %,
Temperature -40.0 °C
 13300 psi

@Strain 6.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Tensile Strength, Yield 65.0 MPa
9430 psi
ISO 527-1/-2
Elongation at Break 23 %
23 %
Nominal; ISO 527-1/-2
Elongation at Yield 11 %
11 %
ISO 527-1/-2
Tensile Modulus 3.00 GPa
435 ksi
ISO 527-1/-2
Flexural Modulus 2.80 GPa
406 ksi
ISO 178
Secant Modulus 0.396 GPa

@Strain 7.00 %,
Temperature 100 °C
 57.4 ksi

@Strain 7.00 %,
Temperature 212 °F
 ISO 11403-1 -2
0.46125 GPa

@Strain 8.00 %,
Temperature 80.0 °C
 66.900 ksi

@Strain 8.00 %,
Temperature 176 °F
 ISO 11403-1 -2
0.595 GPa

@Strain 4.40 %,
Temperature 100 °C
 86.4 ksi

@Strain 4.40 %,
Temperature 212 °F
 ISO 11403-1 -2
0.737 GPa

@Strain 4.60 %,
Temperature 80.0 °C
 107 ksi

@Strain 4.60 %,
Temperature 176 °F
 ISO 11403-1 -2
0.769 GPa

@Strain 2.90 %,
Temperature 100 °C
 112 ksi

@Strain 2.90 %,
Temperature 212 °F
 ISO 11403-1 -2
0.934 GPa

@Strain 7.00 %,
Temperature 23.0 °C
 136 ksi

@Strain 7.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.957 GPa

@Strain 1.40 %,
Temperature 100 °C
 139 ksi

@Strain 1.40 %,
Temperature 212 °F
 ISO 11403-1 -2
1.09 GPa

@Strain 2.30 %,
Temperature 80.0 °C
 158 ksi

@Strain 2.30 %,
Temperature 176 °F
 ISO 11403-1 -2
1.17 GPa

@Strain 8.00 %,
Temperature -40.0 °C
 169 ksi

@Strain 8.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
1.23 GPa

@Strain 0.300 %,
Temperature 100 °C
 179 ksi

@Strain 0.300 %,
Temperature 212 °F
 ISO 11403-1 -2
1.52 GPa

@Strain 0.500 %,
Temperature 80.0 °C
 220 ksi

@Strain 0.500 %,
Temperature 176 °F
 ISO 11403-1 -2
1.53 GPa

@Strain 4.00 %,
Temperature 23.0 °C
 222 ksi

@Strain 4.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
1.89 GPa

@Strain 4.60 %,
Temperature -40.0 °C
 274 ksi

@Strain 4.60 %,
Temperature -40.0 °F
 ISO 11403-1 -2
2.385 GPa

@Strain 2.00 %,
Temperature 23.0 °C
 345.9 ksi

@Strain 2.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
2.73 GPa

@Strain 2.30 %,
Temperature -40.0 °C
 396 ksi

@Strain 2.30 %,
Temperature -40.0 °F
 ISO 11403-1 -2
3.26 GPa

@Strain 0.500 %,
Temperature 23.0 °C
 473 ksi

@Strain 0.500 %,
Temperature 73.4 °F
 ISO 11403-1 -2
3.74 GPa

@Strain 0.500 %,
Temperature -40.0 °C
 542 ksi

@Strain 0.500 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO 180/1A
5.00 kJ/m²

@Temperature -40.0 °C
 2.38 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/1A
Charpy Impact Unnotched 16.0 J/cm²
76.1 ft-lb/in²
ISO 179/1eU
13.0 J/cm²

@Temperature -30.0 °C
 61.9 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Tensile Creep Modulus, 1 hour 2400 MPa

@Time 3600 sec
 348000 psi

@Time 1.00 hour
 ISO 899-1
Tensile Creep Modulus, 1000 hours 1600 MPa

@Time 3.60e+6 sec
 232000 psi

@Time 1000 hour
 ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 120 µm/m-°C
66.7 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 120 µm/m-°C
66.7 µin/in-°F
ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 97.0 °C
207 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 IEC 60695-11-10
HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 IEC 60695-11-10
Descriptive Properties Value Comments
Additives Lubricants
Release agent
Delivery Form Pellets
Part Marking Code >POM-S<
ISO 11469
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification POM-S
ISO 1043
UL recognition UL