- Lubrizol Pellethane® 2363-55DE Thermoplastic Polyurethane Elastomer
Lubrizol Pellethane® 2363-55DE Thermoplastic Polyurethane Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | Pellethane® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Pellethane® 2363-55DE Thermoplastic Polyurethane Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 30 g/10 min @Load 8.70 kg, Temperature 224 °C |
30 g/10 min @Load 19.2 lb, Temperature 435 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 53 | 53 | ASTM D2240 |
| Tensile Strength, Ultimate | 44.8 MPa | 6500 psi | ASTM D412 |
| Elongation at Break | 450 % | 450 % | ASTM D412 |
| 50% Modulus | 0.0117 GPa | 1.70 ksi | ASTM D412 |
| 100% Modulus | 0.0159 GPa | 2.31 ksi | ASTM D412 |
| 300% Modulus | 0.0296 GPa | 4.29 ksi | ASTM D412 |
| Flexural Modulus | 0.152 GPa | 22.0 ksi | ASTM D412 |
| Tear Strength | 105 kN/m | 599 pli | Die C; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 70 | 70 | H22 Wheel, 1000g; ASTM D1044 |
| Compression Set | 30 % @Temperature 25.0 °C, Time 79200 sec |
30 % @Temperature 77.0 °F, Time 22.0 hour |
ASTM D395 |
| 75 % @Temperature 70.0 °C, Time 79200 sec |
75 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395 | |
| Tensile Set | 30 % | 30 % | Elongation set after break; ASTM D412 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 141 µm/m-°C @Temperature -80.0 - -30.0 °C |
78.3 µin/in-°F @Temperature -112 - -22.0 °F |
ASTM D696 |
| Vicat Softening Point | 94.0 °C | 201 °F | 120°C/hr, 9.8N; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 210 °C | 380 - 410 °F | Extrusion |
| 199 - 216 °C | 390 - 420 °F | Molding | |
| Mold Temperature | 15.6 - 60.0 °C | 60.0 - 140 °F | |
| Drying Temperature | 87.8 - 104 °C | 190 - 220 °F | air dew point <-40°C |
Users viewing this material also viewed the following:
- PolyOne Edgetek® X AS/018 White Acrylonitrile Butadiene Styrene (ABS)
- Precision Polymer Engineering C60M Chloroprene Rubber
- Natural Rubber, Not Vulcanized (NR, IR, Polyisoprene)
- Teknor Apex Sinpolene MBW009 Linear Low Density Polyethylene
- Lubrizol ESTANE® 5708F4 Ester Based Thermoplastic Polyurethane (European Grade)
- Arkema Group KYNAR FLEX® 2950-05 Polyvinylidene Fluoride Copolymer - Extrusion & Molding
- 3M Scotch-Weld™ SI40 Surface Insensitive Instant Adhesive
- Haynes 556® alloy, bar after 16000 hours at 871°C (1600°F)
- RheTech Products HP507-01 38% Talc Reinforced High Performance Polypropylene, Non-UV Stabilized, Black
Copyright © lookpolymers.com All Rights Reserved