Lubrizol Isoplast® 202LGF40 Engineering Thermoplastic Polyurethane Resin
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | Isoplast® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Isoplast® 202LGF40 Engineering Thermoplastic Polyurethane Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Available in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 186 MPa | 27000 psi | ASTM D638 |
| Tensile Strength, Yield | 186 MPa | 27000 psi | ASTM D638 |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D638 |
| Elongation at Yield | 1.8 % | 1.8 % | ASTM D638 |
| Tensile Modulus | 12.0 GPa | 1740 ksi | ASTM D638 |
| Flexural Strength | 338 MPa | 49000 psi | ASTM D790 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ASTM D790 |
| Izod Impact, Unnotched | 2.67 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
5.00 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Dart Drop, Total Energy | 14.0 J @Temperature -29.0 °C |
10.3 ft-lb @Temperature -20.2 °F |
ASTM D3763 |
| 17.0 J @Temperature 23.0 °C |
12.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 331 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 144 °C | 291 °F | Unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 138 °C | 280 °F | ASTM D3418 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P2645 TPE, PP Overmold or Standalone use
- 3M Dyneon™ Fluorel™ FE-5621Q Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- Dielectric Polymers NT-100A89 General Purpose Laminating Adhesive (discontinued **)
- Ipiranga Petrochem LB 0120 BPS LLDP
- Mitsubishi Hostaphan® WN, 350 micron Nominal Thickness Translucent White Polyethylene Terephthalate Film
- A. Schulman POLYBATCH™ ASC-331 Inorganic Antislip Masterbatch Based in Polyethylene
- American Elements Tin Oxide Nanopowder
- BASF Ultramid® B3ZG6 BK 30564 30% Glass Filled PA6-1 (Conditioned)
- Beijing Ranger Chem E-52D Liquid Epoxy Resin
- LG Chemical KEYFLEX BT S5035 Ester Type TPE
Copyright © lookpolymers.com All Rights Reserved