Ineos N01G-02 Polypropylene Impact Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer |
| Manufacturer | Ineos Olefins & Polymers USA |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos N01G-02 Polypropylene Impact Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
N01G-02 is a low melt flow rate polypropylene impact copolymer designed for blow molding, extrusion, and compounding applications. The grade benefits from a very high impact resistance at room and low temperatures and a general purpose additive package. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ASTM D792 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 85 | 85 | ASTM D785 |
| Tensile Strength at Break | 16.3 MPa | 2370 psi | 2 in/min; ASTM D638 |
| Tensile Strength, Yield | 25.6 MPa | 3710 psi | 2 in/min; ASTM D638 |
| Elongation at Break | 285 % | 285 % | 2 in/min; ASTM D638 |
| Elongation at Yield | 8.2 % | 8.2 % | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.20 GPa | 174 ksi | 1% Secant; ASTM D790A |
| Izod Impact, Notched | 0.854 J/cm @Temperature -20.0 °C |
1.60 ft-lb/in @Temperature -4.00 °F |
ASTM D256 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 91.7 °C | 197 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.6 °C | 123 °F | ASTM D648 |
| Vicat Softening Point | 151 °C | 304 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 59 % | 59 % | 60° Angle; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Instrumented Impact | Ductile at -20°C | |
| Ductile at 23°C | ||
| Process | Blow Molding | |
| Extrusion | ||
| Region | Mexico | Bamberger Polymers Distribution |
| US & Canada | Bamberger Polymers Distribution |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® 4701-50 Supported Urethane Foam, Firm, PET Supported
- Radici Radilon® S 38F (cond.) Nylon 6
- Magyar Aluminum ALO-DN-4F Alumina
- A. Schulman PP 3490-01G Polypropylene Homopolymer Polypropylene
- A. Schulman POLYFLAM™ RPP 1360 Non-Halogenated Homopolymer Polypropylene
- Epoxyset Epoxiohm EO-21M-5 Electrically Conductive Epoxy Adhesive
- CLAL-MSX DECLAFOR® 1015 TD2 Wire quenched/Cold Rolled Copper Alloy
- Arlon 0.029" (0.7366 mm) Flexible Heater Silicone with Fiberglass Substrate (55579GA028)
Copyright © lookpolymers.com All Rights Reserved