Lubrizol Estane® 2102-65D Thermoplastic Polyurethane Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | ESTANE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Estane® 2102-65D Thermoplastic Polyurethane Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Formerly PellethaneAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0080 cm/cm | 0.0070 - 0.0080 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 |
| Melt Flow | 49 g/10 min @Load 1.20 kg, Temperature 224 °C |
49 g/10 min @Load 2.65 lb, Temperature 435 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Ultimate | 44.1 MPa | 6400 psi | ASTM D412 |
| Elongation at Break | 390 % | 390 % | ASTM D412 |
| 50% Modulus | 0.0165 GPa | 2.39 ksi | ASTM D412 |
| 100% Modulus | 0.0200 GPa | 2.90 ksi | ASTM D412 |
| 300% Modulus | 0.0310 GPa | 4.50 ksi | ASTM D412 |
| Flexural Modulus | 0.255 GPa | 37.0 ksi | ASTM D790 |
| Tear Strength | 263 kN/m | 1500 pli | Die C; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 120 | 120 | H22 Wheel, 1000 g; ASTM D1044 |
| Compression Set | 30 % @Temperature 25.0 °C, Time 79200 sec |
30 % @Temperature 77.0 °F, Time 22.0 hour |
ASTM D395, Method B |
| 40 % @Temperature 70.0 °C, Time 79200 sec |
40 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395, Method B | |
| Tensile Set | 110 % | 110 % | Elongation set after break; ASTM D412 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 120 µm/m-°C @Temperature 20.0 °C |
66.7 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Vicat Softening Point | 142 °C | 288 °F | 120°C/hr, 9.8N; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 - 221 °C | 410 - 430 °F | Molding |
| Mold Temperature | 16.0 - 60.0 °C | 60.8 - 140 °F | |
| Drying Temperature | 99.0 - 110 °C | 210 - 230 °F | air dew point <-40°C |
Users viewing this material also viewed the following:
- Oxford Polymers Oxnilon 66-15-IMP Impact Modified Nylon 66 for Injection Molding
- Lucobit Lucofin® 1411-t1 Polyolefin TPO Granules, White
- SABIC Innovative Plastics NORYL HNA055 PPE+HIPS (Asia Pacific)
- Unipetrol PE HD LITEN® MB/ML 73 HDPE
- Tisan TISOPLEN® 40% Calcite Filled Heat Stabilized Homopolymer Polypropylene
- Formosa Plastics Formolene® 2315N Impact Copolymer Polypropylene
- ExxonMobil Santoprene® 201-64 Thermoplastic Elastomer
- Diamond Polymers Softflex® 8200
- Beijing Evergrow Resources ER-21 UHMW PE Bulletproof Plate
Copyright © lookpolymers.com All Rights Reserved