SABIC Innovative Plastics LNP Lubricomp FX00617 PE (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyethylene (PE) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp FX00617 PE (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* FX00617 is a compound based on Polyethylene resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.990 g/cc | 0.0358 lb/in³ | ASTM D 792 |
| 0.990 g/cc | 0.0358 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.022 cm/cm @Time 86400 sec |
0.022 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.022 cm/cm @Time 86400 sec |
0.022 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm @Time 86400 sec |
0.019 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.019 cm/cm @Time 86400 sec |
0.019 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 8.00 MPa | 1160 psi | ISO 527 |
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ASTM D 638 |
| 9.00 MPa | 1310 psi | ISO 527 | |
| Elongation at Break | 3.6 % | 3.6 % | ISO 527 |
| Elongation at Yield | 14.3 % | 14.3 % | ISO 527 |
| 15.8 % | 15.8 % | ASTM D 638 | |
| Tensile Modulus | 0.300 GPa | 43.5 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 7.00 MPa | 1020 psi | ISO 178 |
| Izod Impact, Notched | 2.67 J/cm @Temperature 23.0 °C |
5.00 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.34 J/cm @Temperature 23.0 °C |
10.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 52.0 kJ/m² @Temperature 23.0 °C |
24.7 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 15.0 J | 11.1 ft-lb | Multiaxial Impact; ISO 6603 |
| 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 171 µm/m-°C @Temperature -40.0 - 40.0 °C |
95.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 171 µm/m-°C @Temperature -40.0 - 40.0 °C |
95.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 195 µm/m-°C @Temperature -40.0 - 40.0 °C |
108 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 196 µm/m-°C @Temperature -40.0 - 40.0 °C |
109 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
Users viewing this material also viewed the following:
- ND Industries 907 Anti-seize Copper-Graphite
- Lehmann & Voss LUVOCOM® 65-8347/RD PP-copolymer, with carbon fiber
- Lucky IG-840 Acrylic, Injection Grade
- Shakespeare S-3 Economy Nylon Copolymer Fishing Line, 15 lb
- Saint-Gobain CHR® 2042-10 Skived PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- SABIC Innovative Plastics NORYL EXNL0353 PPE+HIPS
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 60 PHR Hi-Sil 243 LD Filler
- Fainplast Compounds MPH 85 Medical Flexible PVC, Extrusion
- Radici Radiflam® B RV250AE Polybutylene Terephthalate - 25% Glass fiber reinforced
- LG Chemical HG-174 ABS, High Gloss, Super High Flow
Copyright © lookpolymers.com All Rights Reserved