Lubrizol ESTANE® 58149 Ester Based Thermoplastic Polyurethane
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | ESTANE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol ESTANE® 58149 Ester Based Thermoplastic Polyurethane.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Low Compression SetUse: Hydraulic Seals and Gaskets Available in Americas, Europe, Middle East, Africa, India and AsiaInformation provided by Lubrizol.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 92 - 98 @Time 5.00 sec |
92 - 98 @Time 0.00139 hour |
ASTM D2240 |
| Tensile Strength | 33.9 MPa | 4920 psi | ASTM D412 |
| Elongation at Break | 370 % | 370 % | ASTM D412/D638 |
| 100% Modulus | 0.0135 GPa | 1.96 ksi | ASTM D412 |
| 300% Modulus | 0.0250 GPa | 3.63 ksi | ASTM D412 |
| Tear Strength | 93.6 kN/m | 534 pli | Trouser; ASTM D470 |
| Graves Tear Strength | 109 kN/m | 622 pli | Die C; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 38 | 38 | H18, 1000g; ASTM D3389 |
| Compression Set | 23 % @Temperature 70.0 °C, Time 79200 sec |
23 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395 Method B |
| 37 % @Temperature 100 °C, Time 252000 sec |
37 % @Temperature 212 °F, Time 70.0 hour |
ASTM D395 Method B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | DSC |
| Glass Transition Temp, Tg | -32.0 °C | -25.6 °F | DSC |
| Shrinkage | 0.0080 % @Time 173000 sec |
0.0080 % @Time 48.0 hour |
5" bark |
| 0.0080 % @Time 173000 sec |
0.0080 % @Time 48.0 hour |
4" disk |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 °C | 379 °F | Injection |
| 216 °C | 421 °F | ||
| Middle Barrel Temperature | 204 °C | 399 °F | Injection |
| Nozzle Temperature | 216 °C | 421 °F | Injection |
| Melt Temperature | 216 °C | 421 °F | Injection |
| Drying Temperature | 104 °C | 219 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |
| Dew Point | -40.0 °C | -40.0 °F | |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Injection |
| Hold Pressure | 34.5 - 68.9 MPa | 5000 - 10000 psi | Injection |
| Back Pressure | 0.345 MPa | 50.0 psi | Injection |
| Screw Speed | 20 - 50 rpm | 20 - 50 rpm | Injection |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ BIO 5170D-E0010 Thermoplastic Elastomer (TPE)
- Precision Polymer Engineering N65H Nitrile Rubber
- Parker Chomerics CHO-BOND 1026 Conductive Silicone Splicing Compound
- SABIC Innovative Plastics NORYL GTX GTX909 PPE+PS+PA (Asia Pacific)
- A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66
- ExxonMobil HDPE HTA 001HP2 High Density Polyethylene (HMW) Resin
- Arlon 51149R015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
- NOVA Chemicals Sclair® 8306 BK, 8306G BK MDPE Rotational Molding Resin (discontinued **)
- Outokumpu LDX 2101® Duplex Stainless Steel
- SABIC Innovative Plastics LNP LUBRICOMP QCL349 PA6.10
Copyright © lookpolymers.com All Rights Reserved