- Lubrizol ESTALOC® 59010 Polyester-Type, Reinforced Engineering Thermoplastic Polyurethane
Lubrizol ESTALOC® 59010 Polyester-Type, Reinforced Engineering Thermoplastic Polyurethane
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Glass Filled |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | ESTALOC® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol ESTALOC® 59010 Polyester-Type, Reinforced Engineering Thermoplastic Polyurethane.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Fast Cycling, Dimensional Stability, Durability, Aesthetics, Low Temperature ImpactUses: Injection MoldingAvailability: Americas and AsiaInformation provided by Lubrizol
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | |
| Linear Mold Shrinkage | 0.00070 cm/cm | 0.00070 in/in | flex bar; ASTM D955 |
| 0.0020 cm/cm | 0.0020 in/in | average flow and against flow, disc; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 55 - 61 @Time 5.00 sec |
55 - 61 @Time 0.00139 hour |
ASTM D2240 |
| Tensile Strength | 28.0 MPa | 4060 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Tensile Modulus | 0.621 GPa | 90.0 ksi | ASTM D638 |
| Flexural Strength | 19.0 MPa | 2760 psi | ASTM D790 |
| Flexural Modulus | 0.572 GPa | 83.0 ksi | ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm | 12.0 ft-lb/in | ASTM D256 |
| 0.854 J/cm @Temperature -40.0 °C |
1.60 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C | 124 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 213 °C | 415 °F | Extrusion |
| Middle Barrel Temperature | 218 °C | 424 °F | Extrusion |
| Front Barrel Temperature | 218 °C | 424 °F | Extrusion |
| Nozzle Temperature | 221 °C | 430 °F | Extrusion |
| Melt Temperature | 227 °C | 441 °F | |
| Drying Temperature | 104 °C | 219 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |
| Dew Point | -40.0 °C | -40.0 °F | |
| Injection Pressure | 69.0 - 103 MPa | 10000 - 14900 psi | Extrusion |
| Hold Pressure | 35.0 - 69.0 MPa | 5080 - 10000 psi | Extrusion |
| Back Pressure | 0.345 MPa | 50.0 psi | Extrusion |
| Screw Speed | 30 - 80 rpm | 30 - 80 rpm | Extrusion |
Users viewing this material also viewed the following:
- Nanocyl NANOCYL™ NC7000 Thin Multi-Wall Carbon Nanotubes
- Samsung Cheil Industries Starex® LX-0957 ABS, Unreinforced Metallic-Look
- Teknor Apex APEX® 3311-75 Polyvinyl Chloride, Flexible
- SABIC Innovative Plastics LNP Verton UV00A PPA
- Unitika AXG-1500-300 Dry
- China Tungsten WC 97 Tungsten Carbide Powder
- Daikin NEOFLON AC-5539 PFA Coating Powder, Gray
- China-Yixing Longly Refractories Alumina Plates and Pieces Microcrystal Wear-Resistant Alumina Ceramic Lining Plates and Pieces
- 3M 7214SA Screen Printable Polyester Performance Label Products with Structured Adhesive
Copyright © lookpolymers.com All Rights Reserved