Lubrizol Advanced Materials Pearlthane® Clear 15N60D Thermoplastic Polyurethane (discontinued **)

Category	Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lubrizol Advanced Materials Pearlthane® Clear 15N60D Thermoplastic Polyurethane (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polyester-based TPU, supplied in form of translucent, colorless or slightly yellowish pellets, combining very high hardness with excellent mechanical properties and excellent hyrdrolysis resistance. It is especially advisible for use in producing technical parts by injection molding.Apllications: Technical parts, Injection molding industryInformation provided by Merquinsa

Physical Properties	Metric	English	Comments
Density	1.14 g/cc	0.0412 lb/in³	DIN 53.479
Water Absorption	<= 0.050 %	<= 0.050 %	MQSA 44

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	60	60	DIN 53.505
Tensile Strength, Ultimate	54.0 MPa	7830 psi	DIN 53.504
Elongation at Break	410 %	410 %	DIN 53.504
100% Modulus	0.0200 GPa	2.90 ksi	DIN 53.504
Tear Strength	190 kN/m	1080 pli	DIN 53.517
Abrasion	30	30	mm3; DIN 53516
Compression Set	30 %	30 %	70 hrs @ 23°C; DIN 53.517
	30 % @Temperature 70.0 °C	30 % @Temperature 158 °F	24 hrs @ 70°C; DIN 53.517

Thermal Properties	Metric	English	Comments
Melting Point	220 - 230 °C	428 - 446 °F	MQSA 70, Kofler

Optical Properties	Metric	English	Comments
Transmission, Visible	90 %	90 %	clear; thickness not quantified

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	210 °C	410 °F	Feed Zone
Middle Barrel Temperature	220 °C	428 °F	Compression Zone
Front Barrel Temperature	220 °C	428 °F	Metering Zone
Nozzle Temperature	220 °C	428 °F
Mold Temperature	45.0 °C	113 °F
Drying Temperature	100 - 110 °C	212 - 230 °F