Loxim 100 00V2 Polycarbonate, Flame Retardant
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Loxim Industries |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Loxim 100 00V2 Polycarbonate, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Loxim Industries
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D1299 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D683 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ASTM D638 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790 |
| Izod Impact, Notched | 6.00 - 8.00 J/cm | 11.2 - 15.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 135 - 140 °C | 275 - 284 °F | ASTM D1525, HDT Method B |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- P & P Technology Silicone Sponge
- LG Chemical Lupox® TE5011 PBT+PC
- SABIC Innovative Plastics LNP Lubricomp QP003 PA 6/10 (Asia Pacific)
- SABIC Innovative Plastics NORYL PX2644 PPE+HIPS (Asia Pacific)
- Von Roll Isola IMI Irrathene® 210 Irradiated Polyethylene Film, Encapsulation Grade
- ExxonMobil Bicor™ 70 CSR-M OPP Film
- Alliance N-42H Neodymium Iron Boron Magnetic Material
Copyright © lookpolymers.com All Rights Reserved