- Lord Adhesives 8661 Polymer Resistor Composition
Lord Adhesives 8661 Polymer Resistor Composition
| Category | Polymer , Thermoset |
| Manufacturer | Lord Adhesives |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lord Adhesives 8661 Polymer Resistor Composition.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LORD 8600 series polymer resistor compositions are designed for screen print application onto a wide range of substrates.All information provided by Lord.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Brookfield Viscosity | 20000 - 40000 cP @Temperature 25.0 °C |
20000 - 40000 cP @Temperature 77.0 °F |
HBT, Spindle CP-51 @ 1rpm |
| Thickness | 14.0 - 18.0 microns | 0.551 - 0.709 mil |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistivity per Square | 900000 - 1.10e+6 ohm | 900000 - 1.10e+6 ohm | Cured on alumina substrate @ 210ºC for 30 min; Termination: LORD 3504 Palladium Silver Conductor; Resistor Geometry: 1mm x 1mm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 30.0 min @Temperature 210 °C |
0.500 hour @Temperature 410 °F |
|
| Shelf Life | 6.00 Month @Temperature 25.0 °C |
6.00 Month @Temperature 77.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black | |
| Consistency | Paste | |
| Thermal Coefficient of Resistance (ppm/ºC) | <1300 | Cold TCR measured @ -55 to 25ºC; Hot TCR measured @ 25º to 125ºC |
| Typical Resistance Change (%) | <15 | Moisture Resistance: Resistance change on 1mm x 1mm resistor after 1 hour in a pressure cooker |
| <20 | Electrostatic Discharge: Resistance change after two 2000 volt pulses on 1mm x 1mm resistor |
Users viewing this material also viewed the following:
- Quadrant EPP Duratron® PEI LSG extruded (ISO Data)
- 3M Dyneon™ Fluorel™ FT-2481 Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- Huntsman Araldite GY 9580 Bisphenol A Epoxy Liquid Resin
- Solvay TECHNYL® A 402 Natural FA PA66, Conditioned
- Teknor Apex Sinpolene MBW001LE Low Density Polyethylene
- A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66
- Akzo Nobel Trigonox® EHPS-C75 Polymerization Initiator
- Ascend Performance Materials Vydyne® M344 Nylon 66/6, ignition resistant, Conditioned
- 3M Nextel™ AF-11 w/o sizing Aerospace Woven Fabric 312
Copyright © lookpolymers.com All Rights Reserved