- Lehmann & Voss LUVOCOM® 80-7014 Polyacetal-copolymer, with PTFE
Lehmann & Voss LUVOCOM® 80-7014 Polyacetal-copolymer, with PTFE
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 80-7014 Polyacetal-copolymer, with PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, glide mating with low sliding friction.High dimensionally stable precision parts.Bearings, sleeves, high precision gear wheels, control disks, rollers, coil formers.No mass temperature above 215°C! Ventilation of machinery is recommended.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.47 g/cc | 1.47 g/cc | ISO 1183 |
| Water Absorption | 0.15 % | 0.15 % | 23°C/24h |
| Linear Mold Shrinkage | 0.017 - 0.025 cm/cm | 0.017 - 0.025 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 50.0 MPa | 7250 psi | |
| Elongation at Yield | 10 % | 10 % | |
| 12 % | 12 % | flexural | |
| Modulus of Elasticity | 2.50 GPa | 363 ksi | |
| Flexural Strength | 70.0 MPa | 10200 psi | |
| Flexural Modulus | 2.00 GPa | 290 ksi | |
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | flatwise; ISO 179 1fU |
| Coefficient of Friction, Dynamic | 0.16 | 0.16 | |
| Coefficient of Friction, Static | 0.080 | 0.080 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| 120 °C | 248 °F | short term | |
| Vicat Softening Point | 145 °C | 293 °F | DIN ISO 306 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | mass temp |
| Nozzle Temperature | 175 - 200 °C | 347 - 392 °F | |
| Zone 1 | 175 - 190 °C | 347 - 374 °F | |
| Zone 2 | 185 - 205 °C | 365 - 401 °F | |
| Zone 3 | 180 - 200 °C | 356 - 392 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 7200 - 28800 sec |
167 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| 120 °C @Time 7200 - 14400 sec |
248 °F @Time 2.00 - 4.00 hour |
Air-Circulation Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (white) |
Users viewing this material also viewed the following:
- Indium Corp. 16-1081 Flux Thinner
- Vyncolit Neopreg Kinel® SK61 L5G Glass Fiber Reinforced Molding Compound
- A. Schulman LP479-01 High-Density Polyethylene Homopolymer
- DSM Stanyl® TW200FM33 Nylon 46-30% Glass and Mineral Reinforced (European Grade) (Cond)
- DuPont™ Kapton® 120FN616 Polyimide/FEP Composite Film
- Axiall 53080A Moldings & Extrusions Flexible PVC
- Plastcom SLOVALEN PQ 51 N Polypropylene Homopolymer, Modified with Elastomer, Impacted
Copyright © lookpolymers.com All Rights Reserved