Lehmann & Voss LUVOCOM® 6-7433 Polyamide 12, with carbon fiber, hydrolysis resistant
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 6-7433 Polyamide 12, with carbon fiber, hydrolysis resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Especially suitable at dynamic stress situations.Electrically conductive, suitable for continuous discharging of statically generated electricity.Low waterabsorbtion, for dimensional stable precision parts.Bearings, sleeves, sliding elements, chair rollers, handles.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 125 MPa | 18100 psi | |
| Elongation at Yield | 3.2 % | 3.2 % | |
| 4.2 % | 4.2 % | flexural | |
| Modulus of Elasticity | 9.50 GPa | 1380 ksi | |
| Flexural Strength | 180 MPa | 26100 psi | |
| Flexural Modulus | 8.50 GPa | 1230 ksi | |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
| 140 °C | 284 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1e+05 | <= 1e+05 | |
| Insulation Resistance | <= 100000 ohm | <= 100000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | mass temp |
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |
| Zone 1 | 230 - 250 °C | 446 - 482 °F | |
| Zone 2 | 240 - 260 °C | 464 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 36000 sec |
167 °F @Time 6.00 - 10.0 hour |
Dehumidifying dryer |
| 105 °C @Time <=14400 sec |
221 °F @Time <=4.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P1840P TPE, PP Overmold or Standalone use
- ND Industries Toughened Ethyl SuperGlue 310
- Parker Chomerics Tecknit® 72-00014 Silver-Filled Flexible Resin Caulking System
- Kostat ICP-STAT ICS-1002 PP Sheet
- Mitsubishi Iupilon® S2001R 9.5 MFI FDA Compliant Polycarbonate With Release
- Lubrizol ISOPLAST™ 2560 Engineering Thermoplastic Polyurethane Resin for Medical Applications
- Chosun Refractories A18H Magnesia Carbon Bricks for Electric Arc Furnace
- Arkema Group EVATANE® 28-800 Copolymer Ethylene - Vinyl Acetate
- Arkema Group LOTRYL® 17 BA 04 Copolymer Ethylene - Butyl Acrylate
- Bhansali Engineering Abstron IM-17A(DLW) ABS Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved