Lehmann & Voss LUVOCOM® 50-7586 Polycarbonate, with carbon fiber
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 50-7586 Polycarbonate, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High dimensionally stable precision parts with low warpage and narrow tolerance range.Electrically conductive, suitable for continuous discharging of statically generated electricity.Low influence from moisture and temperature to measures and electrical propertiesEasy demoldability.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ISO 1183 |
| Water Absorption | <= 0.20 % | <= 0.20 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 120 MPa | 17400 psi | |
| Elongation at Yield | 2.8 % | 2.8 % | |
| 3.8 % | 3.8 % | flexural | |
| Modulus of Elasticity | 8.00 GPa | 1160 ksi | |
| Flexural Strength | 165 MPa | 23900 psi | |
| Flexural Modulus | 7.00 GPa | 1020 ksi | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| 150 °C | 302 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 10000 ohm | <= 10000 ohm | |
| Insulation Resistance | <= 10000 ohm | <= 10000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 295 °C | 563 °F | mass temp |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |
| Zone 1 | 280 - 300 °C | 536 - 572 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 300 - 320 °C | 572 - 608 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Reltek BONDiT™ B-45TH Adhesive, Sealant & Coating System
- Advanced Elastomer Systems Santoprene® 8281-35W237 Thermoplastic Rubber (discontinued **)
- Overview of materials for Polyphenylene Ether, Heat Resistant
- Honeywell Aegis™ H135XP Nylon 6 Extrusion Grade Homopolymer Film (discontinued **)
- Haynes 25 alloy, room temperature after 20% cold reduction, 1175°C anneal for 5 minutes
- A. Schulman POLYFLAM™ FPP 1006 Talc Filled Homopolymer Polypropylene
- Zoltek Panex 35® Milled Carbon Fibers
- Eurotec® Tecodur® PB70 GR20 NL100 XA20 PBT, 20% glass fiber reinforced, flame retardant - halogen (RoHS compliant), heat stabilized, natural
- Carlisle 201LL Carbon-Carbon Composite
- Bhansali Engineering Abstron IPM3000 PMMA- ABS Alloy
Copyright © lookpolymers.com All Rights Reserved