Honeywell ACLAR® UltRx 2000 CTFE Homopolymer, Barrier Film
| Category | Polymer , Film , Thermoplastic , Fluoropolymer , Polychlorotrifluoroethylene (PCTFE); Molded |
| Manufacturer | Honeywell |
| Trade Name | ACLAR® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell ACLAR® UltRx 2000 CTFE Homopolymer, Barrier Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: ACLAR® UltRx 2000 is a 2 mil CTFE homopolymer high performance barrier film for the pharmaceutical and medical markets. It thermoforms well on conventional blister packaging equipment.Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.11 g/cc | 2.11 g/cc | ASTM D1505 |
| Density | 2.13 g/cc | 0.0770 lb/in³ | Yield Density |
| Water Vapor Transmission | 0.0190 g/m²/day | 0.00122 g/100 in²/day | 77°F (25°C) / 60%RH; ASTM F1249 |
| 0.0290 g/m²/day | 0.00187 g/100 in²/day | 86°F (30°C) / 65% RH; ASTM F1249 | |
| 0.0390 g/m²/day | 0.00251 g/100 in²/day | 86°F (30°C) / 60%RH; ASTM F1249 | |
| 0.102 g/m²/day | 0.00657 g/100 in²/day | 100°F (37.8°C) / 100%RH; ASTM F1249 | |
| 0.119 g/m²/day | 0.00766 g/100 in²/day | 104°F (40°C) / 75%RH; ASTM F1249 | |
| Thickness | 50.8 microns | 2.00 mil | |
| Surface Tension | >= 42 dynes/cm | >= 42 dynes/cm | treated side; ASTM D2578 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 150 - 200 % | 150 - 200 % | ASTM D882 |
| Film Elongation at Break, TD | 175 - 250 % | 175 - 250 % | ASTM D882 |
| Secant Modulus, MD | 1.172 - 1.38 GPa | 170.0 - 200 ksi | ASTM D882 |
| Secant Modulus, TD | 1.172 - 1.38 GPa | 170.0 - 200 ksi | ASTM D882 |
| Film Tensile Strength at Break, MD | 48.3 - 68.9 MPa | 7000 - 10000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 31.0 - 51.7 MPa | 4500 - 7500 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 211 °C | 412 °F | crystalline melting point; ASTM D4591 |
| Shrinkage, MD | <= 6.0 % | <= 6.0 % | 300°F / 149°C - 10 min.; ASTM D1204 |
| Shrinkage, TD | <= -6.0 % | <= -6.0 % | 300°F / 149°C - 10 min.; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 1.0 % | <= 1.0 % | ASTM D1003 |
Users viewing this material also viewed the following:
- Nyco M3 WOLLASTOCOAT® Wollastonite
- Nye Lubricants UniFlor 8311 (833-1) (UF) Synthetic Oil
- SABIC Innovative Plastics Lexan® DMX9455A PC Copolymer
- Albis Plastics Cellulose Acetate Butyrate B902 (UV Inhibitor Added), 10% Plasticizer (discontinued **)
- Green Dot Terratek® SC 65 Polypropylene - Wheat Starch Biocomposite
- Special Metals NIMONIC® Alloy 80A
- Dow DNDA-8335 NT 7 Linear Low Density Polyethylene Resin
- Cheng Yu Plastic FV30BK Electric Conducting Polyformaldehyde
- Momentive Performance Materials TSE 2287 Heat Cured Rubber - High Duro Translucent
Copyright © lookpolymers.com All Rights Reserved