- Lehmann & Voss LUVOCOM® 3-7901 Polyamide 6, with glass fiber and carbon fiber
Lehmann & Voss LUVOCOM® 3-7901 Polyamide 6, with glass fiber and carbon fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 3-7901 Polyamide 6, with glass fiber and carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, apparatus- and precision engineering.Strong, stiff parts.dynamic stressElectrically conductive, suitable for continuous discharging of statically generated electricity.Handles, levers, rollers, body parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0050 cm/cm | 0.0010 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 165 MPa | 23900 psi | |
| Elongation at Yield | 2.2 % | 2.2 % | |
| 2.5 % | 2.5 % | flexural | |
| Modulus of Elasticity | 14.0 GPa | 2030 ksi | |
| Flexural Strength | 230 MPa | 33400 psi | |
| Flexural Modulus | 24.0 GPa | 3480 ksi | |
| Charpy Impact Unnotched | 4.30 J/cm² | 20.5 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 110 °C | 230 °F | |
| 130 °C | 266 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | 10000 - 1.00e+7 ohm | 10000 - 1.00e+7 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 °C | 518 °F | mass temp |
| Nozzle Temperature | 270 - 280 °C | 518 - 536 °F | |
| Zone 1 | 250 - 270 °C | 482 - 518 °F | |
| Zone 2 | 270 - 290 °C | 518 - 554 °F | |
| Zone 3 | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Drying Temperature | 75.0 °C @Time 36000 - 57600 sec |
167 °F @Time 10.0 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | ocean blue |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 M2 Nylon 6.6 for injection molding, 2% molybdenum disulphide lubricated
- Indium Corp. Indalloy® 3 In-Ag Solder Alloy
- Teknor Apex APEX® RE 8003 Polyvinyl Chloride, Rigid
- Techmer ES Luriblend® PEI GF30 TL15 BK 30% Glass Filled
- SABIC Innovative Plastics LNP THERMOTUF R1000JX4 PA 66 (Asia Pacific)
- Elastocon TPE Technologies Elastocon® 2850PE Thermoplastic Elastomer
- EMS-Grivory Grivory® BKZ-30 PA6-GB30
- Dow ATTANE™ 4401 Ultra Low Density Polyethylene, Blown Film Grade
- DuPont Teijin Films Mylar® A Polyester Film, 142 Gauge
Copyright © lookpolymers.com All Rights Reserved