Braskem Flexus® 9210 LLDPE Blown Film Extrusion  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem Flexus® 9210 LLDPE Blown Film Extrusion  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
25µm film gauge, obtained in 40mm extruder, with blow up ratio 2, 2:1Applications: Automatic packaging (FFS); multilayer packaging films; films for lamination. Information provided by Braskem
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ASTM D1505
Thickness 25.0 microns
0.984 mil
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 44.0 MPa
6380 psi
ASTM D882
Film Tensile Strength at Yield, TD 46.0 MPa
6670 psi
ASTM D882
Film Elongation at Break, MD 870 %
870 %
ASTM D882
Film Elongation at Break, TD 1060 %
1060 %
ASTM D882
Secant Modulus, MD 0.220 GPa
31.9 ksi
1%; ASTM D882
Secant Modulus, TD 0.224 GPa
32.5 ksi
1%; ASTM D882
Coefficient of Friction 0.20
0.20
ASTM D1894
Elmendorf Tear Strength, MD 10.5 g/micron
267 g/mil
ASTM 1922
Elmendorf Tear Strength, TD 17.5 g/micron
445 g/mil
ASTM 1922
Dart Drop 32.8 g/micron
833 g/mil
ASTM D1709
Heat Seal Strength Initiation Temperature 99.0 °C
210 °F
Sealing Initial Temperature
Optical Properties Metric English Comments
Haze 9.0 %
9.0 %
ASTM D1003
Gloss 13 %
13 %
ASTM D2457
Descriptive Properties Value Comments
Additives Antiblock, Slip, and PPA
Puncture Strength 30 J/mm
ASTM D5748