- Lehmann & Voss LUVOCOM® 2205-7123 Blend based on polyaryl ether ketone, with carbon fiber, PTFE, lubricant modified
Lehmann & Voss LUVOCOM® 2205-7123 Blend based on polyaryl ether ketone, with carbon fiber, PTFE, lubricant modified
| Category | Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 2205-7123 Blend based on polyaryl ether ketone, with carbon fiber, PTFE, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: High dimensionally stable precision parts, high continuous use temperature.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceChemical and hydrolysis resistance parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.47 g/cc | 1.47 g/cc | ISO 1183 |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | |
| Melt Flow | 18 g/10 min @Load 10.0 kg, Temperature 380 °C |
18 g/10 min @Load 22.0 lb, Temperature 716 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 145 MPa | 21000 psi | |
| Elongation at Yield | 1.8 % | 1.8 % | |
| 2.3 % | 2.3 % | flexural | |
| Modulus of Elasticity | 13.0 GPa | 1890 ksi | |
| Flexural Strength | 215 MPa | 31200 psi | |
| Flexural Modulus | 11.0 GPa | 1600 ksi | |
| Charpy Impact Unnotched | 2.60 J/cm² | 12.4 ft-lb/in² | flatwise; ISO 179 1fU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 1eA |
| Coefficient of Friction, Dynamic | 0.32 | 0.32 | |
| Coefficient of Friction, Static | 0.29 | 0.29 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 220 °C | 428 °F | |
| 250 °C | 482 °F | short term | |
| Vicat Softening Point | 280 °C | 536 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 370 - 380 °C | 698 - 716 °F | |
| Zone 3 | 380 - 390 °C | 716 - 734 °F | |
| Mold Temperature | 160 - 200 °C | 320 - 392 °F | |
| Drying Temperature | 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | dark grey |
Users viewing this material also viewed the following:
- MV Labs PT465 K2PtCl6 Potassium hexachloroplatinate(IV)
- Rogers Corporation Poron® 4790-92-15 Urethane Foam, Extra Soft, Slow Rebound
- SABIC Innovative Plastics Cycoloy® MC5215 PC+ABS (Asia Pacific)
- PolyOne Geon™ Vinyl Flexible R8570A Polyvinyl Chloride, Flexible (PVC, Flexible)
- PolyOne Geon™ Vinyl Flexible XV3805 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Overview of materials for Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
- Pearl Engineering PEPLPET B-103C PET Bottle Grade
- A. Schulman POLYBATCH™ Grey 8760 Concentrate Based In Polyethylene
- ConocoPhillips ANDEROL® PQ AA 90 White Mineral Food Grade Gear Oil, ISO Grade 220, SAE Gear Oil Grade 90
- 3M Scotchcal™ ElectroCut™ 7125-14 Graphic Film
Copyright © lookpolymers.com All Rights Reserved