- Lehmann & Voss LUVOCOM® 21-7928 Polyamide 6/6T, with carbon fiber, lubricant modified
Lehmann & Voss LUVOCOM® 21-7928 Polyamide 6/6T, with carbon fiber, lubricant modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 21-7928 Polyamide 6/6T, with carbon fiber, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Dynamic stressed parts at high movement velocity.Improved friction and wear behaviour. Emergency running property.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ISO 1183 |
| Water Absorption | <= 0.30 % | <= 0.30 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 135 MPa | 19600 psi | |
| Elongation at Yield | 1.5 % | 1.5 % | |
| 2.0 % | 2.0 % | flexural | |
| Modulus of Elasticity | 13.0 GPa | 1890 ksi | |
| Flexural Strength | 195 MPa | 28300 psi | |
| Flexural Modulus | 11.0 GPa | 1600 ksi | |
| Charpy Impact Unnotched | 2.30 J/cm² | 10.9 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 135 °C | 275 °F | |
| 160 °C | 320 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1.00e+9 ohm | <= 1.00e+9 ohm | |
| Insulation Resistance | <= 1.00e+9 ohm | <= 1.00e+9 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 330 °C | 626 °F | mass temp |
| Nozzle Temperature | 330 - 340 °C | 626 - 644 °F | |
| Zone 1 | 300 - 340 °C | 572 - 644 °F | |
| Zone 2 | 310 - 340 °C | 590 - 644 °F | |
| Zone 3 | 320 - 340 °C | 608 - 644 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 80.0 °C @Time 21600 - 57600 sec |
176 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 110 °C @Time 14400 - 21600 sec |
230 °F @Time 4.00 - 6.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | graphite grey |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP DX00714H PC
- SABIC Innovative Plastics NORYL ZWM2411 PPE+PS (Asia Pacific)
- SMAC SMACSIL® 1114S- S02 Damping Material
- Lubrizol Pellethane® 2363-55D Thermoplastic Polyurethane Elastomer
- TPI Porene® GA300 High Flow Grade, High Gloss ABS
- Covestro Bayblend® T88 GF-10* Polycarbonate + SAN Glass Filled Impact Grade
- DSM Novamid® 2030CA FC PA666
- ArcelorMittal HSLA 460 High strength low alloy steel for cold forming, Hot Rolled
- 3M 8426-11 Cold Shrink Connector Insulators
- BASF Ultramid® B3EG3 BK 00564 15% Glass Filled PA6 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved