- Lehmann & Voss LUVOCOM® 1850-7784 PBT, with glass fiber, glass spheres and PTFE
Lehmann & Voss LUVOCOM® 1850-7784 PBT, with glass fiber, glass spheres and PTFE
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber + PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1850-7784 PBT, with glass fiber, glass spheres and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteristics.Parts for electric and electronic industry.Coil formers, duty parts in plugs and switches, even combined with metal inserts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.61 g/cc | 1.61 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0060 - 0.012 cm/cm | 0.0060 - 0.012 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 57.0 MPa | 8270 psi | |
| Elongation at Yield | 2.7 % | 2.7 % | |
| 3.5 % | 3.5 % | flexural | |
| Modulus of Elasticity | 4.60 GPa | 667 ksi | |
| Flexural Strength | 83.0 MPa | 12000 psi | |
| Flexural Modulus | 4.00 GPa | 580 ksi | |
| Charpy Impact Unnotched | 2.80 J/cm² | 13.3 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| 180 °C | 356 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | mass temp |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | |
| Zone 1 | 240 - 260 °C | 464 - 500 °F | |
| Zone 2 | 260 - 280 °C | 500 - 536 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | |
| Drying Temperature | 80.0 °C @Time 21600 - 28800 sec |
176 °F @Time 6.00 - 8.00 hour |
Vacuum Dryer |
| 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Johnson Matthey GW Platinum w/ 5% Copper Jewelry Alloy
- Sylvin Technologies 9600-75 Clear PVC Molding Compound
- Silberline Silvet® 210-30-E1
- SABIC Innovative Plastics LNP THERMOCOMP 2X00858 FP-F (FEP)
- Chesterton ARC HT-T Spark Testable High Temperature Trowelable Abrasion Control Compound
- ChevronTexaco Syn-Star® GL SAE 75W-90
- Colorite Polymers Flexchem 5551-02 Vinyl Compound
- Bapolene® 122F Polyethylene, Film Grade
- 3M Controltac™ IJ180Cv3-10 Graphic Film with Comply™ Adhesive
- Zhejiang Juner PA-A6-6H High CTI Value Halogen-Free Environmental Protection Flame-Resistant and Reinforced Polyamide
Copyright © lookpolymers.com All Rights Reserved