Lehmann & Voss LUVOCOM® 1700-8541 PPO, unreinforced
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1700-8541 PPO, unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Dynamic stressed parts.Isotropic shrinkage characteristics.Superheated steam sterilizable.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0060 - 0.010 cm/cm | 0.0060 - 0.010 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 65.0 MPa | 9430 psi | |
| Elongation at Yield | 5.2 % | 5.2 % | |
| 7.0 % | 7.0 % | flexural | |
| Modulus of Elasticity | 2.50 GPa | 363 ksi | |
| Flexural Strength | 95.0 MPa | 13800 psi | |
| Flexural Modulus | 2.00 GPa | 290 ksi | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 110 °C | 230 °F | |
| 130 °C | 266 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 280 °C | 536 °F | mass temp |
| Nozzle Temperature | 285 - 295 °C | 545 - 563 °F | |
| Zone 1 | 270 - 280 °C | 518 - 536 °F | |
| Zone 2 | 270 - 300 °C | 518 - 572 °F | |
| Zone 3 | 290 - 305 °C | 554 - 581 °F | |
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | |
| Drying Temperature | 95.0 - 110 °C @Time <=7200 sec |
203 - 230 °F @Time <=2.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | blue |
Users viewing this material also viewed the following:
- Nabaltec NABALOX® NO 625-30 Reactive Alumina
- Premix Premi-Glas® 1200H-25 Fiberglass Reinforced Thermoset SMC
- ExxonMobil LL 6201 Injection Molding Resin (discontinued **)
- Teijin Panlite® LN-2250Y Flame Resistant, Translucent Polycarbonate Resin
- SMAC CABLE® 2519S-30-08 Damping Material
- ThyssenKrupp 75Cr1 Saw Steel, Four-High Mill Plate
- Toyobo NB-5620S Nylon/Olefin Alloy, 15% Mineral Reinforced (DAM)
- A. Schulman POLYBATCH™ Bright Pink 50379 Concentrate Based In Polyethylene
- DuPont Performance Polymers Sorona® 3301 BK001 Polytrimethylene Terephthalate (PTT) (Unverified Data**)&l
Copyright © lookpolymers.com All Rights Reserved