- Lehmann & Voss LUVOCOM® 1301-7767 PPS, linear, with carbon fiber, lubricant modified
Lehmann & Voss LUVOCOM® 1301-7767 PPS, linear, with carbon fiber, lubricant modified
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 10% Carbon Fiber Filler |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1301-7767 PPS, linear, with carbon fiber, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High continuous use and heat distortion temperature. Non flammable.Strong, stiff parts.Suitable for metall inserts.Improved friction and wear behaviour. Emergency running property.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.62 g/cc | 1.62 g/cc | ISO 1183 |
| Water Absorption | <= 0.050 % | <= 0.050 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 115 MPa | 16700 psi | |
| Elongation at Yield | 1.0 % | 1.0 % | |
| 1.35 % | 1.35 % | flexural | |
| Modulus of Elasticity | 13.0 GPa | 1890 ksi | |
| Flexural Strength | 160 MPa | 23200 psi | |
| Flexural Modulus | 11.0 GPa | 1600 ksi | |
| Charpy Impact Unnotched | 1.40 J/cm² | 6.66 ft-lb/in² | flatwise; ISO 179 1fU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 220 °C | 428 °F | |
| 240 °C | 464 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 330 °C | 626 °F | mass temp |
| Nozzle Temperature | 320 - 340 °C | 608 - 644 °F | |
| Zone 1 | 300 - 320 °C | 572 - 608 °F | |
| Zone 2 | 310 - 330 °C | 590 - 626 °F | |
| Zone 3 | 320 - 340 °C | 608 - 644 °F | |
| Mold Temperature | 150 - 180 °C | 302 - 356 °F | |
| Drying Temperature | 50.0 - 90.0 °C @Time >=14400 sec |
122 - 194 °F @Time >=4.00 hour |
|
| 100 - 140 °C @Time 7200 - 14400 sec |
212 - 284 °F @Time 2.00 - 4.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | dark grey |
Users viewing this material also viewed the following:
- ND Industries Toughened Ethyl SuperGlue 310
- Chevron Phillips Ryton® R10 5004A PPS Polyphenylene Sulfide (discontinued **)
- NOVA Chemicals Sclair® 8504 UV8D, 8504G UV8D MDPE Rotational Molding Resin (discontinued **)
- H.C. Starck MP35N® Nickel/Cobalt/Chromium/Molybdenum Alloy
- MRC Polymers NAXALOYâ„¢ 770-BK272 ABS + PC Alloy
- ChevronTexaco Aero 50/Grade 100 Engine Oil AD
- ChevronTexaco ISO 680 AIO
- Cadi 20TC Tungsten Carbide Copper
- Addiplast Addinyl B2 ZM30 Nylon 6, 30% Mineral Filled
- LTL Color Compounds ColorFast® JCT1000 Polycarbonate-ABS-SMA Alloy
Copyright © lookpolymers.com All Rights Reserved