Lehmann & Voss LUVOCOM® 1301-7508 PPS, linear, with glass spheres
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 10% Glass Fiber Filler |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1301-7508 PPS, linear, with glass spheres.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.Strong, stiff parts.High continuous use and heat distortion temperature. Non flammable.High chemical resistance parts.Low warpage, isotropic shrinkage characteristics.Control disks, cams, sliding elements and other duty parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.88 g/cc | 1.88 g/cc | ISO 1183 |
| Water Absorption | <= 0.20 % | <= 0.20 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0060 - 0.013 cm/cm | 0.0060 - 0.013 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 55.0 MPa | 7980 psi | |
| Elongation at Yield | 0.60 % | 0.60 % | |
| 0.80 % | 0.80 % | flexural | |
| Modulus of Elasticity | 12.0 GPa | 1740 ksi | |
| Flexural Strength | 85.0 MPa | 12300 psi | |
| Flexural Modulus | 10.0 GPa | 1450 ksi | |
| Charpy Impact Unnotched | 1.00 J/cm² | 4.76 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 220 °C | 428 °F | |
| 240 °C | 464 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 330 °C | 626 °F | mass temp |
| Nozzle Temperature | 320 - 340 °C | 608 - 644 °F | |
| Zone 1 | 300 - 320 °C | 572 - 608 °F | |
| Zone 2 | 310 - 330 °C | 590 - 626 °F | |
| Zone 3 | 320 - 340 °C | 608 - 644 °F | |
| Mold Temperature | 150 - 180 °C | 302 - 356 °F | |
| Drying Temperature | 50.0 - 90.0 °C @Time >=14400 sec |
122 - 194 °F @Time >=4.00 hour |
|
| 100 - 140 °C @Time 7200 - 14400 sec |
212 - 284 °F @Time 2.00 - 4.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 203R PC (Europe-Africa-Middle East)
- LATI Latamid 66 H-V0 PA 66, Heat Stabilized, Flame Retardant
- Shakespeare LMX-3 Easy Casting Nylon Copolymer Fishing Line, 17 lb
- Teknor Apex APEX® 60002 Polyvinyl Chloride, Flexible
- Plenco 4527 Phenolic, Granular, Injection Molded
- ConocoPhillips Syncon® 50 Synthetic Transmission Oil, ISO Grade
- Carmel Olefins IPETHENE® 4203 Low Density Polyethylene
- Arlon 70011B016 0.016" (0.406 mm) Uncured Silicone Rubber with Prime Coated Polyester Fabric Substrate
- Termopol Termoton® K2GA2060A TPE Compound, based on SEBS and Polyolefins
Copyright © lookpolymers.com All Rights Reserved