Lehmann & Voss LUVOCOM® 1301-7178 PPS, linear, with glass fiber
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 10% Glass Fiber Filler |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1301-7178 PPS, linear, with glass fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High-strength and stiff parts with low creep.High continuous use and heat distortion temperature. Non flammable.High chemical resistance parts.High dimensionally stable precision parts with low warpage and narrow tolerance range.Gear parts for automotive appliances, body parts, grippers, spacers.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ISO 1183 |
| Water Absorption | <= 0.20 % | <= 0.20 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 180 MPa | 26100 psi | |
| Elongation at Yield | 1.7 % | 1.7 % | |
| 2.2 % | 2.2 % | flexural | |
| Modulus of Elasticity | 13.0 GPa | 1890 ksi | |
| Flexural Strength | 260 MPa | 37700 psi | |
| Flexural Modulus | 11.0 GPa | 1600 ksi | |
| Charpy Impact Unnotched | 4.30 J/cm² | 20.5 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 220 °C | 428 °F | |
| 240 °C | 464 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 330 °C | 626 °F | mass temp |
| Nozzle Temperature | 320 - 340 °C | 608 - 644 °F | |
| Zone 1 | 300 - 320 °C | 572 - 608 °F | |
| Zone 2 | 310 - 330 °C | 590 - 626 °F | |
| Zone 3 | 320 - 340 °C | 608 - 644 °F | |
| Mold Temperature | 150 - 180 °C | 302 - 356 °F | |
| Drying Temperature | 50.0 - 90.0 °C @Time >=14400 sec |
122 - 194 °F @Time >=4.00 hour |
|
| 100 - 140 °C @Time 7200 - 14400 sec |
212 - 284 °F @Time 2.00 - 4.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (beige) |
Users viewing this material also viewed the following:
- Chevron Phillips 7109LT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **)
- Shamrock Technologies NanoFLON® P 63B Thermoplastic Grade PTFE Additive
- SABIC Innovative Plastics NORYL PN235 PPE+PS (Asia Pacific)
- A. Schulman POLYFORT™ FPP 1245U CaCO3 Filled UV Stable Copolymer Polypropylene
- Epoxy Technology EPO-TEK® 353ND-T4 Thixotropic Epoxy
- Clariant BRU2000 Nylon 66, Lubricated, Nucleated, Weather Resistant, Black
- Bulk Molding Compounds BMC 5338 Mineral Filled, Glass Reinforced Polyester
- Proto3000 PPSF Fused Deposition Modeling Polymer
- Resirene Resirene® 2210 High Impact Polystyrene
Copyright © lookpolymers.com All Rights Reserved