SABIC Innovative Plastics Noryl EBN3001 PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) , Polystyrene + Polyphenylene Ether, Unreinforced , Polystyrene, Impact Modified |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl EBN3001 PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D 792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | SABIC - Japan Method |
| Elongation at Break | 60 % | 60 % | SABIC - Japan Method |
| Flexural Strength | 66.0 MPa | 9570 psi | ASTM D 790 |
| Flexural Modulus | 2.05 GPa | 297 ksi | ASTM D 790 |
| Izod Impact, Notched | 2.35 J/cm @Temperature 23.0 °C |
4.40 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C @Thickness 3.20 mm |
230 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® N OZO 7039 NBR-PVC blend
- Nitriflex N-5 NBR - Nitrile Rubber
- Glastic Laminates/Shapes 1872 Fiberglass-Reinforced Polyester Standoff Insulator
- MetalTek MAR-M-247® Centri-Vac Nickel Cobalt Based Alloy
- Momentive Performance Materials RTV159 Red Adhesive Sealant, High Strength Paste
- Skamol Group SKAMOLEX V-1100 (800) Customized Shape
- Polyram PlusTek PB340S6 Nylon 6, 30% Glass beads
- Lucent Polymers PPC-0222 Polypropylene, Impact Modified
- Overview of materials for Polypropylene, Extrusion Grade
Copyright © lookpolymers.com All Rights Reserved