LTL Color Compounds ColorFast® PCGF110 Polycarbonate, 10% Glass-Filled
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® PCGF110 Polycarbonate, 10% Glass-Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High modulus 10% glass-filled polycarbonate, V2-rated, general purposeAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | 0.125; ASTM D955 |
| Melt Flow | 9.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
9.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 85 | 85 | ASTM D785 |
| Tensile Strength at Break | 55.2 MPa | 8000 psi | 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 66.2 MPa | 9600 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 15 % | 15 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 103 MPa | 15000 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 3.45 GPa | 500 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 142 °C | 288 °F | Unannealed (0.250"); ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 288 - 310 °C | 550 - 590 °F | |
| Middle Barrel Temperature | 299 - 321 °C | 570 - 610 °F | |
| Front Barrel Temperature | 310 - 332 °C | 590 - 630 °F | |
| Nozzle Temperature | 304 - 327 °C | 580 - 620 °F | |
| Melt Temperature | 310 - 332 °C | 590 - 630 °F | |
| Mold Temperature | 82.2 - 116 °C | 180 - 240 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 48 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00254 - 0.00762 cm | 0.00100 - 0.00300 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- Nilit Nilamid A3 H5 G6 30% Glass Reinforced PA66
- Quadrant EPP TIVAR® Extended Wear UHMW-PE, Premium Glass-filled, Partially Cross-linked (ASTM Product Data Sheet)
- SABIC Innovative Plastics LNP KONDUIT PTF2BXXX PA 6 (Asia Pacific)
- Lubrizol Advanced Materials PEARLBOND® 100 Linear Thermoplastic Polyurethane
- Chosun Refractories LW-30 Special Insulating Firebrick
- Dow Corning 4 ELECTRICAL INSULATING COMPOUND
- Barlog Plastics KEBAFORM C 270 LS black POM Copolymer unreinforced, laser markable
- Chem Polymer Chemlon 113 G Nylon 66, 13% Glass Fiber Reinforced
- 3M 12056 Black 3/16" (4.8 mm) Polyurethane Foam
- Breplast Bretene TS COR HF Film Dark High Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved