LTL Color Compounds ColorFast® PC60 Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® PC60 Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
6 melt extrusion gradeAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | 0.125; ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 70 | 70 | ASTM D785 |
| Tensile Strength at Break | 68.9 MPa | 10000 psi | 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 140 % | 140 % | 2.0 in/min; ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 97.9 MPa | 14200 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 2.34 GPa | 340 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 9.08 J/cm @Temperature 22.8 °C |
17.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | Unannealed (0.250"); ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 288 - 310 °C | 550 - 590 °F | |
| Middle Barrel Temperature | 299 - 321 °C | 570 - 610 °F | |
| Front Barrel Temperature | 310 - 332 °C | 590 - 630 °F | |
| Nozzle Temperature | 304 - 327 °C | 580 - 620 °F | |
| Melt Temperature | 310 - 332 °C | 590 - 630 °F | |
| Mold Temperature | 82.2 - 116 °C | 180 - 240 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 48 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00254 - 0.00762 cm | 0.00100 - 0.00300 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® SOL T 9133 Styrene - Isoprene Block Copolymer
- Abatron AboWeld 8101-9/AboCure 8101-9 Epoxy (discontinued **)
- Mitsui ADMER® QF551A PP Type Polyolefin
- Solvay Specialty Polymers Algoflon® L203F Polytetrafluoroethylene (PTFE)
- SABIC Innovative Plastics LNP STAT-KON SE003 PA 12 (Europe-Africa-Middle East)
- Techmer ES Plastiblend® ABS HH BK MB
- Hexcel® HexForce™ 6581 Fiber Glass Fabric
- Aaron Industries AAROLENE® ARPP H 200-1 Polypropylene Compounded Resin
- Goodfellow Chromium 80/Aluminum 20 Alloy
Copyright © lookpolymers.com All Rights Reserved