LTL Color Compounds ColorFast® FRA204 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® FRA204 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High gloss, excellent impact ABS, V0/5VA-ratedAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | 0.125; ASTM D955 |
| Melt Flow | 8.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
8.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength, Yield | 41.4 MPa | 6000 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 10 % | 10 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 61.4 MPa | 8900 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 2.28 GPa | 330 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 2.67 J/cm @Temperature 22.8 °C |
5.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed (0.250"); ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| 5VA @Thickness 2.60 mm |
5VA @Thickness 0.102 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 171 - 182 °C | 340 - 360 °F | |
| Middle Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Front Barrel Temperature | 210 - 221 °C | 410 - 430 °F | |
| Nozzle Temperature | 193 - 221 °C | 380 - 430 °F | |
| Melt Temperature | 193 - 232 °C | 380 - 450 °F | |
| Mold Temperature | 71.1 - 82.2 °C | 160 - 180 °F | |
| Drying Temperature | 71.1 - 82.2 °C | 160 - 180 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 8 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 50 - 70 % | 50 - 70 % | |
| Vent Depth | 0.00381 - 0.00508 cm | 0.00150 - 0.00200 in | |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| UL File Number | E178307 |
Users viewing this material also viewed the following:
- LyondellBasell Plexar® PX2250 Extrudable Tie-Layer Resin, Anhydride Modified HDPE
- Fine Organics FINALUX G 131 Lubricant Additive
- H.C. Starck Amperit® 250.3 Water Atomized (NiCr 80-20)
- Sibur PVC S-5868-PZ Suspension Polyvinyl Chloride (PVC)
- DuPont Performance Polymers Rynite® FR515 BK507 Polyethylene Terephthalate (PET) (Unverified Data**)
- DuPont Teijin Films Teijin® Tetoron® U4 Polyester Film, 500 Gauge
- Arkema Group Nakan® FEM 781 N PVC, Soft Extrusion Grade
- Arlon 51976R020 0.020" (0.508 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Raschig Group RESINOL® 400 EPF Phenolic
- Fainplast Compounds KLT 75/G Flexible PVC, Sheathing Transparent Cables Lead Free
Copyright © lookpolymers.com All Rights Reserved